Ashley Polymers Ashlene® 520-40G Nylon 66, 40% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 520-40G Nylon 66, 40% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose 40% glass reinforced Nylon 66 resin.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 24 hrs. ASTM D570 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ASTM D570 |
| Water Absorption at Saturation | 4.7 % | 4.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 179 MPa | 26000 psi | ATSM D638 |
| Elongation at Break | 3.0 % | 3.0 % | |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 252 °C | 486 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | ASTM D648 |