Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 484 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
PTS Trimid® N66-G43HL 43% Glass Fiber Reinforced Heat Stabilized, Lubed Nylon 6/6
Information provided by Polymer Technology and Services, LLC (PTS).
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM Data
BASF Capron® 5233G HS BK-102 33% Glass-Filled Nylon 66 (Dry)  (discontinued **)
Capron 5233G HS BK-102 is a 35% glass reinforced, heat stabilized, pigmented black nylon 6,6 injection molding compound offering excellent strength, rigidity, stiffness, creep resistance, and dimens..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RCL34 PA 66
LNP* LUBRICOMP* RCL34 is a compound based on Nylon 66 containing 20% Carbon Fiber, 15% PTFE. Added features of this grade includes: Wear Resistant, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RCL36 is a compound based on PA 66 resin containing PTFE, Carbon Fiber. Added features include: Electrically Conductive, Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RCL36XXP PA 66 (Europe-Africa-Middle East)
LNP* LUBRICOMP* RCL36XXP is a compound based on PA 66 resin, containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66
LNP* LUBRICOMP* RFL16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFN18 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFN18 is a compound based on Nylon 66 resin containing Glass Fiber, MOS2.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Dry)
Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Techmer ES Plaslube® J-1/30/TF/10 Nylon 66, 30% GFR, 10% PTFE
Plaslube glass fiber reinforced, polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer an excellent balance of wear and friction performance and mechanical strength. The addition of silic..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Samyang Tramid® 210G25 Polyamide, Reinforced
Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G25 is a reinforced grade.Applications:Automotive gear level housingConnectors..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C

@Thickness 3.20 mm
484 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66
LNP* THERMOCOMP* RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RX10408H PA 66
LNP* Thermocomp* RX10408H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP UFW49RS PPA (Europe-Africa-Middle East)
LNP* Thermocomp* UFW49RS is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C

@Thickness 3.20 mm
484 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 (Asia Pacific)
LNP VERTON* RVL28 is a compound based on Nylon 66 resin containing Long Glass Fiber, PTFE. Added features of this material include: Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RX89047 PA 66
LNP* VERTON* RX89047 is a compound based on Nylon 66 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 (Asia Pacific)
LNP* Verton* RX89047 is a compound based on Nylon 66 resin.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 (Europe-Africa-Middle East)
LNP* Verton* RX89047 is a compound based on Nylon 66 resin.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
Unannealed; ISO 75-2/A
Ascend Performance Materials Vydyne® R535H NT651 Nylon 66, 35% Glass Reinforced, DAM
Vydyne® R535H NT651 is 35% glass-fiber reinforced PA66 resin. Available in natural, it is heat-stabilized with an electrically neutral heat stabilizer. It is designed specially for electrical appli..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Ashley Polymers Ashlene® 528L-30LG Nylon 66, 30% Long Glass Fiber Reinforced
Long glass fiber reinforced Nylon 66 designed for parts requiring excellent thermal and dimensional stability and higher strength than available with conventional glass reinforced resins.Data provid..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman ComAlloy Voloy® 682 Nylon 6/6, Glass Fiber, Nylon 6/6 Alloy, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Ashley Polymers Ashlene® 520-40G Nylon 66, 40% Glass Reinforced
A general purpose 40% glass reinforced Nylon 66 resin.Data provided by the manufacturer
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
A. Schulman ComAlloy Lubrilon® 635 Nylon 6/6, Carbon Fiber/PTFE Filled, Proprietary Lubricant Package
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Deflection Temperature at 1.8 MPa (264 psi) 251 °C

@Thickness 3.20 mm
484 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Verton RX93407D PA 66
LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Plenco 1510 Polyester, Granular, Transfer Molded
PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file ..