Ascend Performance Materials Vydyne® R525 Nylon 66, 25% Glass Reinforced, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R525 Nylon 66, 25% Glass Reinforced, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R525 is hydrolysis-resistant, 25% glass-fiber reinforced PA66 resin. Available in natural it is lubricated for improved machine feed and flow. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 25% Filler by WeightAdditive:Lubricant Features: Antifreeze ResistanceFatigue ResistantGasoline ResistanceGood FlowHeat StabilizedHydrolysis ResistantLubricatedOil ResistantSolvent ResistantUses:Automotive Under the Hood Appearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 0.90 %

@Time 86400 sec
0.90 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.0 %
2.0 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Diameter 2.00 mm
0.0040 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Diameter 2.00 mm
0.0090 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 117 MPa
17000 psi
ISO 527-2
Elongation at Break 7.0 %
7.0 %
ISO 527-2
Tensile Modulus 5.50 GPa
798 ksi
ISO 527-2
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 5.70 GPa
827 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 6.60 J/cm²

@Temperature -30.0 °C
31.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
6.70 J/cm²

@Temperature 23.0 °C
31.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA