- Asahi Kasei Thermylene® P-20TC-1156 Chemically Coupled Polypropylene Compound, 20% Talc Filled
Asahi Kasei Thermylene® P-20TC-1156 Chemically Coupled Polypropylene Compound, 20% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P-20TC-1156 Chemically Coupled Polypropylene Compound, 20% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive: Blower Wheels, HVAC Electrical and Specialty: Flush Valves, Pump BasesInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 15 g/10 min | 15 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | |
| Elongation at Yield | 18 % | 18 % | |
| Flexural Modulus | 2.34 GPa | 340 ksi | |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Polymist® F-5 PTFE Powder Lubricant (discontinued **)
- Hong Kun Group 2-Bromo-5-methylbenzotrifluoride Pharmaceutical Intermediate
- KKPC Kuhmo HI 450S High Gloss HIPS
- Guarniflon PTFE G418 Polytetrafluoroethylene 15% Glass Fiber, 5% Molybdenum Disulfide
- Karina 811-18/466-Y-CRB Gray PVC Compound
- Sekisui PIOCELAN LSP-40EB Moldable Polymer Foam
- CoorsTek ACI-Co6 Tungsten Carbide
- A. Schulman ComAlloy Comtuf® 152 Polypropylene, Mineral Reinforced, Impact Modified
- AlphaGary Evoprene™ COGEE 683 SEBS Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved