Armstrong X-6/E Epoxy Adhesive
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Armstrong Epoxy Adhesives; Resin Technology Group |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Armstrong X-6/E Epoxy Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thixotropic.Information provided by Ellsworth Adhesives.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 | 89 | |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | after optimum cure |
| Elongation at Break | 2.7 % | 2.7 % | |
| Adhesive Bond Strength | 41.0 MPa | 5950 psi | Steel-Steel; after optimum cure |
| 12.8 MPa @Temperature 25.0 °C |
1850 psi @Temperature 77.0 °F |
Aluminum-Aluminum tensile shear | |
| 13.4 MPa @Temperature 82.2 °C |
1950 psi @Temperature 180 °F |
Aluminum-Aluminum tensile shear | |
| 13.4 MPa @Temperature -54.4 °C |
1950 psi @Temperature -66.0 °F |
Aluminum-Aluminum tensile shear |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
|
| Glass Transition Temp, Tg | 92.0 °C | 198 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F |
| Pot Life | <= 4320 min @Temperature 25.0 °C |
<= 4320 min @Temperature 77.0 °F |
100 g |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Grey | |
| Mix Ratio | 40/1 | By Weight |