Polymer Property : Rupture Strength = 41.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	41.0 MPa @Temperature 750 °C, Time 3.60e+7 sec	5950 psi @Temperature 1380 °F, Time 10000 hour
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Rupture Strength	41.0 MPa @Temperature 750 °C, Time 3.60e+7 sec	5950 psi @Temperature 1380 °F, Time 10000 hour
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Rupture Strength	41.0 MPa @Temperature 927 Â°C, Time 3.60e+6 sec	5950 psi @Temperature 1700 Â°F, Time 1000 hour
Haynes 282Â® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Rupture Strength	41.0 MPa @Temperature 760 Â°C, Time 360000 sec	5950 psi @Temperature 1400 Â°F, Time 100 hour	Typical Stress-Rupture
Haynes 75 Nickel Alloy Sheet, Annealed at 1925Â°F (1050Â°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200Â°F (650Â°C). It is principally used in low stress elevated temperature applications requiring reas..
Rupture Strength	41.0 MPa @Temperature 927 Â°C, Time 3.60e+6 sec	5950 psi @Temperature 1700 Â°F, Time 1000 hour	Sheet
Special Metals UDIMETÂ® alloy 188 Cobalt-base Alloy UDIMETÂ® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000Â°F (1093Â°C). The high chromium level coupled with small ..
Rupture Strength	41.0 MPa @Temperature 800 °C, Time 3.60e+7 sec	5950 psi @Temperature 1470 °F, Time 10000 hour	Stress Rupture
AFE Technologies Cronite 25Cr/20Ni No. HR6 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF..
Rupture Strength	41.0 MPa @Temperature 927 °C, Time 3.60e+6 sec	5950 psi @Temperature 1700 °F, Time 1000 hour
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..