- A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 4.486 GPa | 650.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.98 J/cm | 3.71 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Osprey Metals 410L Stainless Steel Powder (Grade 80% - 22)
- PolyMirae Moplen HP552N Fiber (Staple) Grade Polypropylene
- Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced
- A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound
- Chosun Refractories A18H Magnesia Carbon Bricks for Electric Arc Furnace
- Asia International Enterprise (Hong Kong) 60G7F Nylon 66, 35% Filled
- DSM Stanyl® TQ261F5 PA46-GF25
- H.C. Starck Amperit® 552.072 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni)
Copyright © lookpolymers.com All Rights Reserved