Polymer Property : Melt Flow = 2.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 1.2 - 2.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
1.2 - 2.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Polyplastic Armoflen® PO MF 65-3 Polyethylene, 65% Mineral Filled
50% Calcium Carbonate / 15% Titanium Oxide FilledInformation provided by PolyPlastic Group.
Melt Flow 1.5 - 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.5 - 2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 4240G (EP2S29B) Propylene and Ethylene Copolymer
Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow 1.0 - 2.0 g/10 min
1.0 - 2.0 g/10 min
Kazanorgsintez 107-18 Composition of Low Density Polyethylene, Crack-Proof
Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow 1.0 - 2.0 g/10 min
1.0 - 2.0 g/10 min
Kazanorgsintez 107-19 Composition of Low Density Polyethylene, Crack-Proof
Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow 1.0 - 2.0 g/10 min
1.0 - 2.0 g/10 min
Kazanorgsintez 107-20 Composition of Low Density Polyethylene, Crack-Proof
Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow 1.0 - 2.0 g/10 min
1.0 - 2.0 g/10 min
Kazanorgsintez 107-22 Composition of Low Density Polyethylene, Crack-Proof
Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod..
Melt Flow 1.5 - 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.5 - 2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Kazanorgsintez PE2NT74-15 High Density Polyethylene for Blow Molding
Production Method: Gaseous-phase method. Application: Compositions are intended for goods produced by injection molding method.Information Provided by Kazanorgsintez
Melt Flow 1.8 - 2.0 g/10 min

@Load 2.61 kg,
Temperature 190 °C
1.8 - 2.0 g/10 min

@Load 5.75 lb,
Temperature 374 °F
ASTM D1238
LG Chemical SEETEC BF410 LDPE
Characteristics: Good Processability and Excellent Optical PropertiesAdditives: Antiblocking Agent, Slip AgentApplications: Industrial Film & Food PackageCAS No. 9002-88-4Information provided by LG ..
Melt Flow 1.6 - 2.0 g/10 min

@Load 2.61 kg,
Temperature 190 °C
1.6 - 2.0 g/10 min

@Load 5.75 lb,
Temperature 374 °F
ASTM D1238
LG Chemical SEETEC BF415 LDPE
Characteristics: Good Processability and Excellent Optical Properties Applications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical
Melt Flow 1.0 - 2.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
1.0 - 2.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
GRECO ISOPAK 525 ABS Resin
General Purpose Injection GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd.
Melt Flow 0.80 - 2.0 g/10 min
0.80 - 2.0 g/10 min
Shandong Dongyue Shenzhou New Material Co DS602 Perfluorinated Ethylene-Propylene Copolymer
Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and..
Melt Flow 0.80 - 2.0 g/10 min
0.80 - 2.0 g/10 min
Shandong Dongyue Shenzhou New Material Co DS606 Fluorinated Ethylene Propylene Powder
Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene powder is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, an..
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.
Melt Flow 0.70 - 2.0 g/10 min
0.70 - 2.0 g/10 min
ASTM D1238
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene
DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman.