Overview of materials for Fluorocarbon ETFE, with Glass or Carbon Fiber Filler

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , Fluorocarbon ETFE, with Glass or Carbon Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Fluorocarbon ETFE, with Glass or Carbon Fiber Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Fluorocarbon ETFE, with Glass or Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.66 - 1.92 g/cc
0.0600 - 0.0694 lb/in³
Average value: 1.77 g/cc Grade Count:15
Filler Content 10.0 - 30.0 %
10.0 - 30.0 %
Average value: 21.9 % Grade Count:8
Water Absorption 0.0100 - 0.0200 %
0.0100 - 0.0200 %
Average value: 0.0140 % Grade Count:5
Additive Loading 10.0 - 30.0 %
10.0 - 30.0 %
Average value: 20.0 % Grade Count:5
Linear Mold Shrinkage 0.000500 - 0.00800 cm/cm
0.000500 - 0.00800 in/in
Average value: 0.00304 cm/cm Grade Count:14
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 21.0 - 75.8 MPa
3050 - 11000 psi
Average value: 56.7 MPa Grade Count:15
Elongation at Break 0.550 - 78.0 %
0.550 - 78.0 %
Average value: 12.1 % Grade Count:15
Modulus of Elasticity 1.51 - 19.3 GPa
219 - 2800 ksi
Average value: 9.90 GPa Grade Count:14
Flexural Yield Strength 24.0 - 103 MPa
3480 - 15000 psi
Average value: 82.9 MPa Grade Count:15
Flexural Modulus 1.21 - 17.2 GPa
175 - 2500 ksi
Average value: 7.83 GPa Grade Count:15
Izod Impact, Notched 0.747 - 8.01 J/cm
1.40 - 15.0 ft-lb/in
Average value: 3.27 J/cm Grade Count:15
Izod Impact, Unnotched 2.14 - 16.0 J/cm
4.00 - 30.0 ft-lb/in
Average value: 8.37 J/cm Grade Count:15
Thermal Properties Metric English Comments
CTE, linear 24.0 - 80.0 µm/m-°C
13.3 - 44.4 µin/in-°F
Average value: 52.7 µm/m-°C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 50.0 - 210 °C
122 - 410 °F
Average value: 169 °C Grade Count:8
Flammability, UL94 V-0
V-0
Grade Count:9
Electrical Properties Metric English Comments
Electrical Resistivity 100 - 1.00e+17 ohm-cm
100 - 1.00e+17 ohm-cm
Average value: 5.00e+16 ohm-cm Grade Count:9
Surface Resistance 1000 - 1.00e+9 ohm
1000 - 1.00e+9 ohm
Average value: 1.23e+8 ohm Grade Count:5
Static Decay 0.500 - 2.00 sec
0.500 - 2.00 sec
Average value: 0.875 sec Grade Count:4
Processing Properties Metric English Comments
Processing Temperature 274 - 335 °C
525 - 635 °F
Average value: 304 °C Grade Count:8
Melt Temperature 293 - 343 °C
560 - 650 °F
Average value: 318 °C Grade Count:5
Mold Temperature 65.6 - 149 °C
150 - 300 °F
Average value: 107 °C Grade Count:13
Drying Temperature 121 °C
250 °F
Average value: 121 °C Grade Count:5
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:13