- Polytetrafluoroethylene (PTFE), Conductive Carbon Filled
- 3M Dyneon™ CC191-HE PTFE, 25% Carbon/Graphite Filled (discontinued **)
3M Dyneon™ CC191-HE PTFE, 25% Carbon/Graphite Filled (discontinued **)
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Conductive Carbon Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Dyneon™ CC191-HE PTFE, 25% Carbon/Graphite Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Form: Black, non-pelletized powder. Applications include bearings, bushings.Data provided by Dyneon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.04 g/cc | 0.0737 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | value after 15 sec; ASTM D2240 |
| 68 | 68 | initial value; ASTM D2240 | |
| Tensile Strength, Ultimate | 13.1 MPa | 1900 psi | ASTM D4745 |
| Elongation at Break | 120 % | 120 % | ASTM D4894 |
| Flexural Yield Strength | <= 29.0 MPa | <= 4210 psi | ASTM D790 |
| Compressive Yield Strength | 10.5 MPa | 1520 psi | ASTM D695 |
| Compressive Modulus | 0.600 GPa | 87.0 ksi | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | ASTM D3702 |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D3702 |
| K (wear) Factor | 15.1 x 10-8 mm³/N-M | 7.50 x 10-10 in³-min/ft-lb-hr | at 5000 psi - fpm PV; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 144 µm/m-°C @Temperature 20.0 °C |
80.0 µin/in-°F @Temperature 68.0 °F |