| Peel Strength |
0.09861 kN/m |
0.5625 pli |
Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.110 kN/m |
0.625 pli |
HD Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.1205 kN/m |
0.6875 pli |
LD Polypropylene, 90° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.1205 kN/m |
0.6875 pli |
LD Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.1424 kN/m |
0.8125 pli |
Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.175 kN/m |
1.00 pli |
HD Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.23008 kN/m |
1.3125 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.23008 kN/m |
1.3125 pli |
HD Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.2849 kN/m |
1.625 pli |
LD Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.307 kN/m |
1.75 pli |
LD Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.31773 kN/m |
1.8125 pli |
LD Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.351 kN/m |
2.00 pli |
HD Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.3725 kN/m |
2.125 pli |
HD Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.3725 kN/m |
2.125 pli |
HD Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.42729 kN/m |
2.4375 pli |
LD Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.51494 kN/m |
2.9375 pli |
Polypropylene, 180° Peel, initial 10 min dwell at RT; ASTM D3330 |
| |
0.570 kN/m |
3.25 pli |
Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |