Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 19.7 - 24.0 kV/mm | 500 - 610 kV/in | Average value: 21.1 kV/mm Grade Count:3 |
Overview of materials for Polypropylene with 20% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are .. |
|||
Dielectric Strength | 19.7 - 24.0 kV/mm | 500 - 610 kV/in | Average value: 22.3 kV/mm Grade Count:5 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Dielectric Strength | 17.7 - 24.0 kV/mm | 450 - 610 kV/in | Average value: 21.0 kV/mm Grade Count:4 |
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Dielectric Strength | 13.8 - 24.0 kV/mm | 350 - 610 kV/in | Average value: 16.0 kV/mm Grade Count:6 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Dielectric Strength | 16.9 - 24.0 kV/mm | 430 - 610 kV/in | Average value: 21.2 kV/mm Grade Count:4 |
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ.. |
|||
Dielectric Strength | 7.44 - 24.0 kV/mm | 189 - 610 kV/in | ASTM D149 |
Zeus PTFE Tubing Zeus offers a wide range of standard size products and precision custom PTFE Tubing. PTFE Tubing has become the gold standard in industries requiring the ultimate in lubricity, high temperature use,.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON M-300H PCTFE Granular Molding Powder NEOFLON PCTFE M-300 series is used for general purpose applications.Description:Granular powders.Processing Methods: Compression molding, extrusion.Uses: Sheets, rods, tubing.Information provided by.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON M-300P PCTFE Pellets NEOFLON PCTFE M-300 series is used for general purpose applications.Description:Pellets.Processing Methods: Extrusion.Uses: Rods, small parts.Information provided by Daikin Industries. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON M-400H PCTFE Granular Molding Powder NEOFLON PCTFE M-400 series is a high molecular weight type material which is suitable for applications requiring mechanical toughness and stress crack resistance.Description:Granular powders.Process.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-101 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: High speed wire and cable coatings.Information pro.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-120 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, cable jacketing, tubes.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-130 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-21 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Suited to high speed extrusion .. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-30 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, tubes, cable jacketing.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-40 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, transfer molding, compression molding.Applications: Films and s.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-20 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding, injection molding.Applications: Wire and cable coatings, films,.. |
|||
Dielectric Strength | 20.0 - 24.0 kV/mm @Thickness 3.20 mm |
508 - 610 kV/in @Thickness 0.126 in |
Short time; ASTM D149 |
Daikin NEOFLON NP-3000 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Ultra high speed wire and cable coatings.Information provi.. |
|||
Dielectric Strength | 19.7 - 24.0 kV/mm | 500 - 610 kV/in | Average value: 21.4 kV/mm Grade Count:7 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |
|||
Dielectric Strength | 12.0 - 24.0 kV/mm @Temperature 95.0 - 200 °C |
305 - 610 kV/in @Temperature 203 - 392 °F |
Average value: 18.9 kV/mm Grade Count:2 |
Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 30% Glass Reinforced". Specific grades with glass content between 25% .. |
|||
Dielectric Strength | 12.0 - 24.0 kV/mm @Thickness 1.57 - 3.20 mm |
305 - 610 kV/in @Thickness 0.0618 - 0.126 in |
Average value: 18.9 kV/mm Grade Count:2 |
Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 30% Glass Reinforced". Specific grades with glass content between 25% .. |
|||
Dielectric Strength | 18.0 - 24.0 kV/mm | 457 - 610 kV/in | Average value: 22.5 kV/mm Grade Count:11 |
Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Unreinforced, Extruded". Each property range of values reported is minimum .. |