Polymer Property : Cure Time = 1080 min Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
NextGen Adhesives P907-04 Fiber Optic Adhesive Description: NGAC P907-04 is a low viscosity and room temperature curing adhesive specifically formulated for fiber optic terminations.Advantages and Applications: Uses include the termination of si..
Cure Time	1080 - 1440 min @Temperature 23.0 °C	18.0 - 24.0 hour @Temperature 73.4 °F
Master Bond EP30 Optically Clear, Low Viscosity Two Component Epoxy Master Bond Polymer System EP30 is a low viscosity, two component epoxy system for high performance bonding, coating, sealing, potting and encapsulation. It readily cures at room temperature or more..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
Tra-Con Tra-Bond F113SC BLK High Tg Fiber Optic Epoxy Adhesive TRA-BOND F113SC BLK is a fiber optic adhesive used for terminating ALL types of fiber optic connectors as well as LED displays, lenses and other optical components. It produces a typical Tg of 95°C..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
Tra-Con Tra-Bond F113SC High Tg Fiber Optic Epoxy Adhesive TRA-BOND F113SC is a room temperature curing, high Tg and low viscosity adhesive formulated for terminating ALL TYPES of fiber optic connectors. It has also been used for bonding LED displays, lense..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
Tra-Con Tra-Bond F118 Fiber Optic Epoxy Adhesive TRA-BOND F118 is an impact resistant, fiber-optic adhesive designed for use in any optical connector. This two-part epoxy remains at a constant viscosity for a minimum of 30 minutes. This allows mor..
Cure Time	1080 - 1440 min @Temperature 23.9 °C	18.0 - 24.0 hour @Temperature 75.0 °F	ambient temperatures
Master Bond EP40 High Shear and Peel Strength, Two Component, Flexible Epoxy Master Bond Polymer System EP40 is newly developed two component highly flexible epoxy compound for high performance bonding, potting, encapsulation, and sealing with outstanding shear and peel stre..
Cure Time	1080 - 1440 min @Temperature 23.0 °C	18.0 - 24.0 hour @Temperature 73.4 °F
Master Bond Supreme 11 High Peel and Shear Strength Epoxy Adhesive Master Bond Polymer System Supreme 11 features a unique balance of performance properties including both high shear and high peel strengths. This two component adhesive system is formulated to cure ..
Cure Time	1080 - 1440 min @Temperature 23.0 °C	18.0 - 24.0 hour @Temperature 73.4 °F
Master Bond Supreme 11HT High Temperature Resistant Two Component Epoxy System Master Bond Polymer System Supreme 11HT is an easy to use two part epoxy adhesive/sealant combining both high shear and high peel strengths along with a relatively fast cure at room temperature. Sup..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
Tra-Con Tra-Bond F131 High Tg Room Temperature Cure Fiber Optic Adhesive TRA-BOND F131 is a fiber-optic adhesive used for terminating ALL types of fiber-optic connectors as well as LED displays, lenses and other optical components. It produces a typical Tg of 95°C thus ..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton ARC HT-T Spark Testable High Temperature Trowelable Abrasion Control Compound An advanced ceramic composite formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. This system is a high viscosity composite that is applied b..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton ARC MXHT High temperature severe wear compound Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness o..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F	Light Load
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F	Light Load
Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton ARC S2 Ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% soli..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton MRS S2 Metal Rebuilding System An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% solids. MRS S2 is..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F	Light Load
Chesterton MRS S4+ Metal Rebuilding System An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375 microns (15 ..
Cure Time	1080 min @Temperature 16.0 °C	18.0 hour @Temperature 60.8 °F	Light Load
Chesterton MRS SD4i Metal Rebuilding System An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F	Overcoat End
Chesterton ARC HT-S High Temperature Corrosion Resistant Coating Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with ..
Cure Time	1080 min @Temperature 32.0 °C	18.0 hour @Temperature 89.6 °F	Full Chemical
Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F
Atom Adhesives AA-BOND F131 Epoxy Adhesive AA-BOND F131 is two parts fiber-optic adhesive used for terminating ALL types of fiber-optic connectors as well as LED displays, lenses and other optical components. AA-BOND F131 produces a typical ..
Cure Time	1080 min @Temperature 25.0 °C	18.0 hour @Temperature 77.0 °F	Light Load
Chesterton ARC S4+ 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375..
Cure Time	1080 min @Temperature 32.0 °C	18.0 hour @Temperature 89.6 °F	Light Load
Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating An advanced composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1-2 mm (40-80 mils) per coat. However, greater si..