Chesterton ARC MXHT High temperature severe wear compound

Category Ceramic , Polymer , Thermoset , Epoxy
Manufacturer Chesterton
Trade Name ARC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC MXHT High temperature severe wear compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness of 6mm (1/4”) or more. It is a 100% solids, non-shrinking coating. ARC MXHT is formulated with a high concentration of ceramic breads and fine ceramic particles for extremely abrasive environments where superior protection is needed. ARC MXHT is applied to a primed surface by trowel. It is chosen over ARC MX1 when abrasion resistance at elevated temperature is required. Benefits:Outlasts other wear resistant materials and coatings by 5-7 timesExcellent wear characteristics extend equipment’s operating cyclesOutperforms weld overlay or ceramic tilesTough resin structure resists thermal-mechanical shock.Use in pH range 2-14 up to 130°C/266°F (wet service) and 230°C/466°F (dry service)No need to post cure Suggested Uses:
Physical Properties Metric English Comments
Density 2.90 g/cc
0.105 lb/in³
Cured
Mechanical Properties Metric English Comments
Hardness, Shore D 89
89
ASTM D2240
Tensile Strength at Break 29.6 MPa
4300 psi
ASTM D638
Elongation at Break 0.10 %
0.10 %
ASTM D638
Flexural Strength 55.8 MPa
8100 psi
ASTM D790
Flexural Modulus 4.83 GPa
701 ksi
ASTM D790
Compressive Strength 162 MPa
23500 psi
ASTM D695
Adhesive Bond Strength >= 13.8 MPa
>= 2000 psi
ASTM D4541
Impact Test 13.6 J
10.0 ft-lb
Reverse; ASTM D2794
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Wet Service
230 °C
446 °F
Dry Service
Processing Properties Metric English Comments
Cure Time 180 min

@Temperature 32.0 °C
3.00 hour

@Temperature 89.6 °F
Tack Free
240 min

@Temperature 25.0 °C
4.00 hour

@Temperature 77.0 °F
Tack Free
360 min

@Temperature 32.0 °C
6.00 hour

@Temperature 89.6 °F
Light Load
480 min

@Temperature 16.0 °C
8.00 hour

@Temperature 60.8 °F
Tack Free
540 min

@Temperature 25.0 °C
9.00 hour

@Temperature 77.0 °F
Light Load
1080 min

@Temperature 16.0 °C
18.0 hour

@Temperature 60.8 °F
Light Load
4320 min

@Temperature 32.0 °C
72.0 hour

@Temperature 89.6 °F
Full Mechanical/Chemical
5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Full Mechanical/Chemical
10100 min

@Temperature 16.0 °C
168 hour

@Temperature 60.8 °F
Full Mechanical/Chemical
Descriptive Properties Value Comments
Color Black