Overview of materials for Polychlorotrifluoroethylene; Molded

Category Polymer , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polychlorotrifluoroethylene; Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polychlorotrifluoroethylene; Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 2.16 g/cc
0.0434 - 0.0780 lb/in³
Average value: 2.03 g/cc Grade Count:22
Water Absorption 0.000 %
0.000 %
Average value: 0.000 % Grade Count:4
Water Vapor Transmission 0.00470 - 0.780 g/m²/day
0.000303 - 0.0502 g/100 in²/day
Average value: 0.161 g/m²/day Grade Count:15
0.00780 - 0.0650 g/m²/day

@Temperature 30.0 - 40.0 °C
0.000502 - 0.00419 g/100 in²/day

@Temperature 86.0 - 104 °F
Average value: 0.0314 g/m²/day Grade Count:2
Oxygen Transmission 3.00 - 9.77 cc-mm/m²-24hr-atm
7.62 - 24.8 cc-mil/100 in²-24hr-atm
Average value: 4.69 cc-mm/m²-24hr-atm Grade Count:4
27.6 - 27.6 cc-mm/m²-24hr-atm

@Temperature 40.0 - 40.0 °C
70.1 - 70.1 cc-mil/100 in²-24hr-atm

@Temperature 104 - 104 °F
Average value: 27.6 cc-mm/m²-24hr-atm Grade Count:1
Nitrogen Transmission 0.500 cc-mm/m²-24hr-atm
1.27 cc-mil/100 in²-24hr-atm
Average value: 0.500 cc-mm/m²-24hr-atm Grade Count:3
Viscosity 1.00e+11 - 1.00e+11 cP

@Temperature 230 - 230 °C
1.00e+11 - 1.00e+11 cP

@Temperature 446 - 446 °F
Average value: 1.00e+11 cP Grade Count:3
Thickness 15.2 - 203 microns
0.600 - 8.00 mil
Average value: 57.4 microns Grade Count:12
Linear Mold Shrinkage 0.0150 - 0.0200 cm/cm
0.0150 - 0.0200 in/in
Average value: 0.0175 cm/cm Grade Count:3
Surface Tension 42.0 dynes/cm
42.0 dynes/cm
Average value: 42.0 dynes/cm Grade Count:7
Mechanical Properties Metric English Comments
Hardness, Shore D 72.0 - 90.0
72.0 - 90.0
Average value: 79.6 Grade Count:7
Tensile Strength, Ultimate 31.0 - 42.1 MPa
4500 - 6100 psi
Average value: 36.9 MPa Grade Count:7
13.0 - 16.0 MPa

@Temperature 120 - 120 °C
1890 - 2320 psi

@Temperature 248 - 248 °F
Average value: 14.5 MPa Grade Count:2
Tensile Strength, Yield 3.00 - 6.00 MPa

@Temperature 120 - 120 °C
435 - 870 psi

@Temperature 248 - 248 °F
Average value: 4.50 MPa Grade Count:2
Film Elongation at Break, MD 70.0 - 250 %
70.0 - 250 %
Average value: 149 % Grade Count:15
Film Elongation at Break, TD 150 - 325 %
150 - 325 %
Average value: 233 % Grade Count:15
Elongation at Break 37.0 - 250 %
37.0 - 250 %
Average value: 151 % Grade Count:7
Modulus of Elasticity 1.00 - 2.06 GPa
145 - 298 ksi
Average value: 1.49 GPa Grade Count:6
Flexural Modulus 1.27 - 1.76 GPa
185 - 256 ksi
Average value: 1.47 GPa Grade Count:5
Compressive Yield Strength 9.00 - 45.0 MPa
1310 - 6530 psi
Average value: 20.2 MPa Grade Count:5
Secant Modulus, MD 0.448 - 1.65 GPa
65.0 - 240 ksi
Average value: 1.21 GPa Grade Count:15
Secant Modulus, TD 0.448 - 1.55 GPa
65.0 - 225 ksi
Average value: 1.18 GPa Grade Count:15
Izod Impact, Notched 0.758 - 0.800 J/cm
1.42 - 1.50 ft-lb/in
Average value: 0.786 J/cm Grade Count:3
Izod Impact, Unnotched 1.33 - 1.44 J/cm
2.49 - 2.70 ft-lb/in
Average value: 1.38 J/cm Grade Count:3
Coefficient of Friction 0.260 - 0.600
0.260 - 0.600
Average value: 0.390 Grade Count:4
Coefficient of Friction, Static 0.0800 - 0.800
0.0800 - 0.800
Average value: 0.235 Grade Count:4
Tear Strength Test 275 - 525
275 - 525
Average value: 377 Grade Count:8
Taber Abrasion, mg/1000 Cycles 40.0 - 48.0
40.0 - 48.0
Average value: 42.7 Grade Count:3
Film Tensile Strength at Break, MD 26.2 - 141 MPa
3800 - 20500 psi
Average value: 62.3 MPa Grade Count:15
Film Tensile Strength at Break, TD 17.9 - 62.1 MPa
2600 - 9000 psi
Average value: 39.2 MPa Grade Count:15
Thermal Properties Metric English Comments
CTE, linear 45.0 - 70.0 µm/m-°C
25.0 - 38.9 µin/in-°F
Average value: 55.4 µm/m-°C Grade Count:6
250 - 250 µm/m-°C

@Temperature 70.0 - 150 °C
139 - 139 µin/in-°F

@Temperature 158 - 302 °F
Average value: 250 µm/m-°C Grade Count:2
Thermal Conductivity 0.135 - 0.220 W/m-K
0.937 - 1.53 BTU-in/hr-ft²-°F
Average value: 0.195 W/m-K Grade Count:12
Melting Point 210 - 212 °C
410 - 414 °F
Average value: 211 °C Grade Count:14
Maximum Service Temperature, Air 120 - 200 °C
248 - 392 °F
Average value: 153 °C Grade Count:7
Flammability, UL94 V-0
V-0
Grade Count:3
Oxygen Index 95.0 - 100 %
95.0 - 100 %
Average value: 98.6 % Grade Count:11
Optical Properties Metric English Comments
Haze 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 1.23 % Grade Count:15
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 - 1.20e+18 ohm-cm
1.00e+16 - 1.20e+18 ohm-cm
Average value: 4.86e+17 ohm-cm Grade Count:5
Dielectric Constant 2.30 - 3.00
2.30 - 3.00
Average value: 2.51 Grade Count:5
Dielectric Strength 15.0 - 200 kV/mm
381 - 5080 kV/in
Average value: 57.8 kV/mm Grade Count:6
Dissipation Factor 0.0100 - 0.0270
0.0100 - 0.0270
Average value: 0.0175 Grade Count:3