SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| 1.111 g/cc | 0.04014 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.380 % | 0.380 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0038 cm/cm @Time 86400 sec |
0.0038 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
| 66.0 MPa | 9570 psi | ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Tensile Modulus | 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 |
| 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| 107 MPa | 15500 psi | ISO 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | ASTM D790 |
| 4.50 GPa | 653 ksi | ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP6GF50 Nylon 6, 50% Glass Reinforced, Conditioned
- Gromax CFG45-RN13N1 Nylon 6 46% Glass Filled (Conditioned)
- Saint-Gobain CHR® SG16-06(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Suzhou Hipro Polymers Hiprolon® 200 NN Nylon 1010, conditioned
- DuPont Elvaloy® 1913 AC Ethylene and 13% Methyl Acrylate Copolymer
- Chevron Phillips MarFlex® 5430 Low Density Polyethylene, Cast Film
- Dow Corning SZ-1325E Silicone Surfactant
- ELASTO UK Dryflex® 422351S SBS Based Material, 35D Hardness, Black
- 3M Dyneon™ TF 9205 PTFE
Copyright © lookpolymers.com All Rights Reserved