SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
| 96.0 MPa | 13900 psi | ASTM D 638 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D 638 |
| Elongation at Yield | 1.9 % | 1.9 % | ASTM D 638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
| 145 MPa | 21000 psi | ASTM D 790 | |
| Flexural Modulus | 6.21 GPa | 901 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C |
0.693 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.47 J/cm @Temperature 23.0 °C |
6.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D 257 |
Users viewing this material also viewed the following:
- Polymer Resources PC/ABS-G20 General Purpose PC/ABS Alloy, 20% Glass Filled
- Styron CALIBREâ„¢ 280-15 Polycarbonate
- Tra-Con Tra-Bond F123NC High Temperature Fiber Optic Epoxy Adhesive
- A. Schulman FORMION™ FI 301 Ionomer
- ExxonMobil LDPE LD 258 Low Density Polyethylene Resin (European Grade)
- ExxonMobil Paxon™ AL55-003 Blow Molding Resin
- Dow ATTANE™ 4401 Ultra Low Density Polyethylene, Blown Film Grade
- CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Dry
- KKPC KOSYN KSL 5153 Styrene-Butadiene Latex
Copyright © lookpolymers.com All Rights Reserved