Polymer Resources PPX-FRG10 Modified-PPO, V-1 Flame Retardant, 10% Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled , Polyphenylene Ether, Heat Resistant
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FRG10 Modified-PPO, V-1 Flame Retardant, 10% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified-Polyphenylene Oxide, V-1 Flame Retardant, 10% Glass ReinforcedFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Linear Mold Shrinkage 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Melt Flow 1.0 - 8.0 g/10 min

@Load 11.6 kg,
Temperature 250 °C
1.0 - 8.0 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 104
104
ASTM D785
Tensile Strength at Break 75.8 MPa
11000 psi
ASTM D638
Tensile Strength, Yield 77.2 MPa
11200 psi
ASTM D638
Elongation at Break 5.0 %
5.0 %
ASTM D638
Flexural Strength 117 MPa
16900 psi
ASTM D790
Flexural Modulus 3.72 GPa
540 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm

@Temperature -40.0 °C
1.30 ft-lb/in

@Temperature -40.0 °F
ASTM D256
0.854 J/cm

@Temperature 22.8 °C
1.60 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Charpy Impact, Notched 0.630 J/cm²

@Temperature 22.8 °C
3.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
ASTM D648
Vicat Softening Point 146 °C
295 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.50 mm
149 °F

@Thickness 0.0591 in
UL 746
65.0 °C

@Thickness 3.00 mm
149 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-1

@Thickness 1.50 mm
V-1

@Thickness 0.0591 in
V-1

@Thickness 3.00 mm
V-1

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 299 °C
480 - 570 °F
Middle Barrel Temperature 260 - 304 °C
500 - 580 °F
Front Barrel Temperature 271 - 310 °C
520 - 590 °F
Melt Temperature 282 - 310 °C
540 - 590 °F
Mold Temperature 76.7 - 98.9 °C
170 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001