- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 177 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 177 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Lubri-Tech™ PF-000/15T Polysulfone, PTFE Lubricated
(discontinued **) Description/Features:PTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 7466 Phenolic, Nodular, Injection Molded
(discontinued **) Two-Stage Phenolic. PLENCO 07466 is a flock cotton and mineral filled phenolic molding compound offering excellent heat resistance and dimensional stability. UL recognized under component file E406.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 202 Black General Purpose Woodflour Filled Phenolic Molding Compound
(discontinued **) Plaslok 202 is a two-stage, woodflour-filled phenolic molding compound formulated to provide improved impact and fatigue strength, good dimensional stability and excellent molded finish for automoti.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 5440 Black General Purpose Phenolic Molding Compound
(discontinued **) Plaslok 5440 is the replacement material for the former Union Carbide BMRS-5440. It is a two-stage, phenolic molding compound that has been successfully formulated to accommodate a very wide range .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 501 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 501 is a two-stage, mineral and flock-filled phenolic molding compound designed for use in heat resistant and electrical applications. It is designed for elevated temperature exposure for e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plaslok 202 Black General Purpose Woodflour Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 202 is a two-stage, woodflour-filled .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plaslok 301 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 301 is a two-stage, woodflour and flo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ISO 75-1,-2 |
| Gromax BFM30-EL04B2 Nylon 6 30% Mineral Filled (Conditioned) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_NC3508 PPE+HIPS (Europe-Africa-Middle East) PRELIMINARY DATA. LNP* Stat-kon* Noryl_NC3508 compound is a 33% glass/mineral/carbon filled PPE+PS. ESD, high heat, tight tolerance: electronic packaging/chip trays. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 AF Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid FiberAdditive: Heat Stabilizer and LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and Heat StabilizedInformat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Sumitomo Bakelite Durez® 153 Phenolic, Compression Grade Durez 153 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits good molded appearance and shock resistance for use on a wide variety of electrical a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY WF306C PBT LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11 LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PSU TL20 Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 2369 Phenolic, Granular, Transfer Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |
| TriStar CJ Composite Bearing This family of materials offers the combination of high compressive strength, low coefficient of friction, and excellent abrasion and corrosion resistance while running without lubrication. They are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Staramide PF004EUC PA6, 20% Glass Filled, Injection Molded PF004EUC is a 20% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | |
| Saint-Gobain Rulon® FCJ Grade Bearing/Seal PTFE
(discontinued **) Saint Gobain Rulon® CJ is now produced as a part of the TriStar Plastics Corp. product line under the CJ Bearings trade name.Description: Rulon® is the Saint-Gobain trade name for their family of .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| ALM PA 601-CF Filled Nylon 12 Prototyping Polymer Carbon fiber filled nylon 12 easy to process, strong light weight filled material.Low density, good dimensional stability while maintaining excellent mechanical properties.Fibers have been optimized.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Plenco 301 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 301 is a two-stage, woodflour and flock-filled phenolic molding compound. It has broad molding latitude combined with good electrical properties and improved impact strength. It is particu.. |
|||