Plaslok 202 Black General Purpose Woodflour Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Woodflour Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plaslok 202 Black General Purpose Woodflour Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 202 is a two-stage, woodflour-filled phenolic molding compound formulated to provide improved impact and fatigue strength, good dimensional stability and excellent molded finish for automotive, electrical and mechanical applications.Data provided by Plaslok Corporation.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Apparent Bulk Density 0.560 g/cc
0.0202 lb/in³
ASTM D1895
Water Absorption 0.40 %
0.40 %
ASTM D570
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D638
Flexural Yield Strength 76.0 MPa
11000 psi
ASTM D790
Flexural Modulus 8.30 GPa
1200 ksi
ASTM D790
Compressive Yield Strength 221 MPa
32100 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.63 mm
302 °F

@Thickness 0.0642 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.63 mm
302 °F

@Thickness 0.0642 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.63 mm
302 °F

@Thickness 0.0642 in
Flammability, UL94 V-1
V-1
3.12 mm
V-1
V-1
3.12mm
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 4.8
4.8
1MHz; ASTM D150
6.0
6.0
60 Hz; ASTM D150
Dielectric Strength 11.8 kV/mm
300 kV/in
ASTM D149
Dissipation Factor 0.040
0.040
1 MHz; ASTM D150
0.10
0.10
60 Hz; ASTM D150
Comparative Tracking Index 125 V
125 V
UL 746