ALM PA 601-CF Filled Nylon 12 Prototyping Polymer

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled
Manufacturer ALM Advanced Laser Materials
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ALM PA 601-CF Filled Nylon 12 Prototyping Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Carbon fiber filled nylon 12 easy to process, strong light weight filled material.Low density, good dimensional stability while maintaining excellent mechanical properties.Fibers have been optimized to produce a smooth surface finish without sacrificing feature detail for tensile properties.Excellent choice for rugged industrial applications with an HDT of ~177° C.Information provided by Advanced Laser Materials (ALM).
Physical Properties Metric English Comments
Bulk Density 0.440 g/cc
0.0159 lb/in³
ASTM D1895
Density 1.07 g/cc
0.0387 lb/in³
Sintered; ASTM D792
Particle Size 50 µm
50 µm
D50
35 - 100 µm
35 - 100 µm
D10-D90
Melt Flow 50 g/10 min

@Load 5.00 kg,
Temperature 235 °C
50 g/10 min

@Load 11.0 lb,
Temperature 455 °F
3 min; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 66.0 MPa
9570 psi
XY; ASTM D638
Elongation at Break 3.6 %
3.6 %
XY; ASTM D638
Tensile Modulus 2.896 GPa
420.0 ksi
XY; ASTM D638
Flexural Modulus 3.447 GPa
499.9 ksi
XY; ASTM D790
Izod Impact, Notched 0.540 J/cm
1.01 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 184 °C
363 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 178 °C
352 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 7.80e+14 ohm-cm
7.80e+14 ohm-cm
50% RH, 500V; ASTM D257
Surface Resistance 2.90e+14 ohm
2.90e+14 ohm
50% RH, 500V; ASTM D257