Toyobo GLAMIDE® T-802 Nylon-6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Toyobo
Trade Name GLAMIDE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo GLAMIDE® T-802 Nylon-6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-802 is a soft type, non-reinforced Nylon-6 used in high-cycles.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
Absolute Drying; ASTM-D792
Water Absorption 2.3 %
2.3 %
Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium 3.5 %
3.5 %
Absolute Drying; ASTM-D570
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 1.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.0394 in
Absolute Drying
0.012 - 0.014 cm/cm

@Thickness 3.00 mm
0.012 - 0.014 in/in

@Thickness 0.118 in
Absolute Drying
Melt Flow 55 g/10 min
55 g/10 min
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
Absolute Drying; ASTM-D785
Tensile Strength, Ultimate 20.0 MPa

@Temperature 80.0 °C
2900 psi

@Temperature 176 °F
Practical Use (Water Absorption 3.5%); ASTM-D638
30.0 MPa

@Temperature 80.0 °C
4350 psi

@Temperature 176 °F
Absolute Drying; ASTM-D638
35.0 MPa

@Temperature 23.0 °C
5080 psi

@Temperature 73.4 °F
Practical Use (Water Absorption 3.5%); ASTM-D638
80.0 MPa

@Temperature 23.0 °C
11600 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D638
100 MPa

@Temperature -40.0 °C
14500 psi

@Temperature -40.0 °F
Practical Use (Water Absorption 3.5%); ASTM-D638
110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D638
Elongation at Break 115 %
115 %
Absolute Drying; ASTM-D638
>= 200 %
>= 200 %
Practical Use (Water Absorption 3.5%); ASTM-D638
Flexural Strength 25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
40.0 MPa

@Temperature 80.0 °C
5800 psi

@Temperature 176 °F
Absolute Drying; ASTM-D790
50.0 MPa

@Temperature 23.0 °C
7250 psi

@Temperature 73.4 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
103 MPa

@Temperature 23.0 °C
14900 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
125 MPa

@Temperature -40.0 °C
18100 psi

@Temperature -40.0 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
130 MPa

@Temperature -40.0 °C
18900 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Flexural Modulus 0.400 GPa

@Temperature 80.0 °C
58.0 ksi

@Temperature 176 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
0.800 GPa

@Temperature 80.0 °C
116 ksi

@Temperature 176 °F
Absolute Drying; ASTM-D790
1.00 GPa

@Temperature 23.0 °C
145 ksi

@Temperature 73.4 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
2.70 GPa

@Temperature 23.0 °C
392 ksi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
3.30 GPa

@Temperature -40.0 °C
479 ksi

@Temperature -40.0 °F
Practical Use (Water Absorption 3.5%); ASTM-D790
3.60 GPa

@Temperature -40.0 °C
522 ksi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Compressive Strength 82.0 MPa
11900 psi
Absolute Drying; ASTM-D695
Izod Impact, Notched 0.350 J/cm

@Temperature -40.0 °C
0.656 ft-lb/in

@Temperature -40.0 °F
Absolute Drying; ASTM-D256
0.500 J/cm

@Temperature -40.0 °C
0.937 ft-lb/in

@Temperature -40.0 °F
Practical Use (Water Absorption 3.5%); ASTM-D256
0.540 J/cm

@Temperature 23.0 °C
1.01 ft-lb/in

@Temperature 73.4 °F
Absolute Drying; ASTM-D256
4.00 J/cm

@Temperature 23.0 °C
7.49 ft-lb/in

@Temperature 73.4 °F
Practical Use (Water Absorption 3.5%); ASTM-D256
Taber Abrasion, mg/1000 Cycles 5.0
5.0
CS-17, Absolute Drying; ASTM-D1044
Thermal Properties Metric English Comments
CTE, linear 84.0 µm/m-°C
46.7 µin/in-°F
Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Absolute Drying; ASTM-D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+8 - 1.00e+9 ohm-cm
1.00e+8 - 1.00e+9 ohm-cm
Practical Use (Water Absorption 3.5%); ASTM-D257
1.00e+12 ohm-cm
1.00e+12 ohm-cm
Absolute Drying; ASTM-D257
Dielectric Constant 3.8

@Frequency 1000 Hz
3.8

@Frequency 1000 Hz
Absolute Drying; ASTM-D150
8.0

@Frequency 1000 Hz
8.0

@Frequency 1000 Hz
Practical Use (Water Absorption 3.5%); ASTM-D150
Dielectric Strength 12.0 kV/mm

@Thickness 2.00 mm
305 kV/in

@Thickness 0.0787 in
Practical Use (Water Absorption 3.5%); ASTM-D149
18.0 kV/mm

@Thickness 2.00 mm
457 kV/in

@Thickness 0.0787 in
Absolute Drying; ASTM-D149
Dissipation Factor 0.020

@Frequency 1000 Hz
0.020

@Frequency 1000 Hz
Absolute Drying; ASTM-D150
Arc Resistance 105 sec
105 sec
Practical Use (Water Absorption 3.5%); ASTM-D495
125 sec
125 sec
Absolute Drying; ASTM-D495
Comparative Tracking Index >= 600 V
>= 600 V
IEC Method
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
Injection Pressure 30.0 - 40.0 MPa
4350 - 5800 psi