Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigidity. High compressive strength. Good thermal properties. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.UL classification: UL94 HB (3,05mm) RTI(C) 110/105/110Example applications: Quick connectors.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Melt Flow 4.8 g/10 min

@Load 2.16 kg,
Temperature 235 °C
4.8 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 108 MPa
15700 psi
5 mm/min
Elongation at Break 5.0 %
5.0 %
5 mm/min
Tensile Modulus 7.43 GPa
1080 ksi
1 mm/min
Charpy Impact Unnotched 7.70 J/cm²
36.6 ft-lb/in²
6.39 J/cm²

@Temperature -30.0 °C
30.4 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.63 J/cm²
7.76 ft-lb/in²
0.980 J/cm²

@Temperature -30.0 °C
4.66 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 20.0 °C
27.8 µin/in-°F

@Temperature 68.0 °F
Melting Point 174 °C
345 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Vicat Softening Point 165 °C
329 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 45.0 kV/mm
1140 kV/in
Comparative Tracking Index 600 V
600 V