- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 257 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 257 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T8038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® BFL2000 PC (Asia Pacific) Non-Brominated, non-chlorinated flame retardant PC. Available in opaque white colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T1040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Geloy XTPM307 ASA+PC (Europe-Africa-Middle East) XTPM307 is a high heat resistant PC/ASA with improved processing stability over HRA150. Typical values measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® EXRL0684 PC Copolymer 7 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Hyosung Topilene J301CP PP J301CP Injection Special Purpose GradeApplications: Cap of pressure bottleCharacteristics:High stiffnessSlip propertyInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa MAC-601 UV PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic partsComputer and accessoriesHou.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Unannealed; ASTM D648 |
| Global PP-2340-TC Polypropylene Block Copolymer Description-opacity, medium to high stiffness, high impact strength at low temperatureApplications-electrical appliances, bases, panels, auto parts, cupsInformation provided by Global Polymers Corp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| IRPC Polimaxx Polene 2340TC Polypropylene Block Copolymer CHARACTERISTICS: EXCELLENT FLOWABILITY, HIGH STIFFNESS, MEDIUM IMPACT, HEAT STABILITYAPPLICATIONS: INJECTION MOLDING FOR THIN WALL CONTAINERS : DRINKING CUPS, NOODLE CUPS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| LG Chemical LUPOL SO-5202P High Impact Polypropylene, 20% Polymer Alloy LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| LATI Latilon 28D PC Polycarbonate (PC). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability. Very good surface appearanceAvailability: Africa & Middle East; Asia Pacific; Europe; Latin A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Asia Pacific) Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP D7002IXH PC LNP* THERMOCOMP* D7002IXH is a compound based on Polycarbonate siloxane copolymer resin containing proprietary antimicrobial additives. Designed for touch surfaces, housings, etc., in healthcare an.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene DescriptionPolyfort® FPP 1902 HU is a 10% talc fortified polypropylene. It exhibits high flow and is stabilized for UV resistance. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Tipco Tipcolene® CR 8229 - 20% Talc/Mineral Reinforced Polypropylene Copolymer Compound with Controlled Rheology 20% Mineral Reinforced, High Flow & Controlled Rheology PP CopolymerApplications: Automotive Door TrimsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
I.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | GB1634 |
| Zhejiang Juner JEPPB003 High Glossy PP Applications: Electric Rice CookerInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | DIN 53461 |
| Polyram PlusTek PD100 Nylon 12, Injection Molding Outstanding polyamide 12 for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Cheng Yu Plastic SW15 POM/PTFE |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® L 20 LM PA12 Product Description: Grilamid L 20 LM is a medium viscosity Polyamide 12 (PA12) extrusion grade. Grilamid L 20 LM is UV and heat stabilized and has been modified with a nucleation agent which result.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 140 °C | 257 - 284 °F | ASTM D648 |
| Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 140 °C | 257 - 284 °F | ASTM D648 |
| Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339T30L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 140 °C | 257 - 284 °F | ASTM D648 |
| Arkema Group KYNAR® 720, 720 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T5038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1006S is a 20% talc filled homopolymer polypropylene compound formulated with an internal mold release. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| LATI LARIL 13-V1 Polyphenylene Oxide (PPOm) (UL94V-1)
(discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| LATI Latene® 9H TES/30 PP Homopolymer, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Heat stabilized. Aesthetic talc.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind.. |
|||