LATI Latene® 9H TES/30 PP Homopolymer, Heat Stabilized

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® 9H TES/30 PP Homopolymer, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Aesthetic talc.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Linear Mold Shrinkage, Flow 0.0105 - 0.0135 cm/cm
0.0105 - 0.0135 in/in
Linear Mold Shrinkage, Transverse 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 10.0 MPa

@Temperature 60.0 °C
1450 psi

@Temperature 140 °F
20.0 MPa

@Temperature 23.0 °C
2900 psi

@Temperature 73.4 °F
Elongation at Break 30 %

@Temperature 23.0 °C
30 %

@Temperature 73.4 °F
70 %

@Temperature 60.0 °C
70 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
Elongation at Yield 4.0 %

@Temperature 23.0 °C
4.0 %

@Temperature 73.4 °F
5.0 %

@Temperature 60.0 °C
5.0 %

@Temperature 140 °F
6.0 %

@Temperature 90.0 °C
6.0 %

@Temperature 194 °F
Tensile Modulus 0.650 GPa

@Temperature 90.0 °C
94.3 ksi

@Temperature 194 °F
1.20 GPa

@Temperature 60.0 °C
174 ksi

@Temperature 140 °F
2.70 GPa

@Temperature 23.0 °C
392 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.0700 J/cm²

@Temperature -20.0 °C
0.333 ft-lb/in²

@Temperature -4.00 °F
0.200 J/cm²

@Temperature 23.0 °C
0.952 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 120 °C
248 °F
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 100 °C

@Load 5.00 kg
212 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 200 - 240 °C
392 - 464 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa