- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 172 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 172 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C @Thickness 3.18 mm |
342 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ 600 A Zip 22 Natural Polyamide 6 Alloy (Nylon 6 Alloy) The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYshine PBT D223 Q30 FR PBT, Mineral Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized
(discontinued **) Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Asahi Kasei Tenac® 5012 Acetal Homopolymer
(discontinued **) Standard-flow grade, with reduced stiffness and increased elongation through addition of special polymers.Applications: Clips, fasteners, press-fit parts.This product is not a part of the standard p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **) 25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Asahi Kasei Tenac® LT805 Acetal Homopolymer, Low Friction Grade
(discontinued **) Excellent friction and wear on metals.Applications: Keyboard parts, bearings for office machines, gears.This product is not a part of the standard product line dated 2003. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | |
| Covestro Apec® DP 1-9359/7 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer M.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ISO 75-1,-2 |
| Lanxess Durethan® BC 30 S 000000 Nylon 6 PA 6, non-reinforced, injection moldingInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C @Thickness 3.20 mm |
342 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON EX02598C PEI LNP* STAT-KON* EX02598C is a compound based on Polyetherimide containing Proprietary Filler(s). Added features of this material include: Clean Compound System, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C @Thickness 6.40 mm |
342 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX905 PPE+PS+PA Automotive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ISO 75-1/-2 |
| Covestro Apec® 1897 Polycarbonate Easy flowingeasy to demoldUV-stabilizedsoftening temperature (VST/B 120)=182 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 662 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | |
| Covestro Apec® 1805 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionCoatingBlow moldingCalanderingTransfer moldingThermoformingInformation pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C @Thickness 3.20 mm |
342 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9353 High-Heat Polycarbonate, UV Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||