Polykemi AB POLYshine PBT D223 Q30 FR PBT, Mineral Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Mineral Filled
Manufacturer Polykemi AB
Trade Name POLYshine
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYshine PBT D223 Q30 FR PBT, Mineral Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0050 - 0.0090 cm/cm
0.0050 - 0.0090 in/in
With Flow; ISO 2577
0.0050 - 0.0090 cm/cm
0.0050 - 0.0090 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 55.0 MPa
<= 7980 psi
ISO/R527
Elongation at Break 4.0 %
4.0 %
ISO/R527
Flexural Strength <= 85.0 MPa
<= 12300 psi
ISO 178
Flexural Modulus 4.40 GPa

@Temperature 23.0 °C
 638 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 172 °C
342 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
181 °F
120°C/h; ISO 75/1
Vicat Softening Point 175 °C

@Load 5.001 kg
 347 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 695-2-1