Lanxess Durethan® BC 30 S 000000 Nylon 6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BC 30 S 000000 Nylon 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, injection moldingInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.122 g/cc
0.04053 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
60x60x2; 270°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
at yield, conditioned, 50 mm/min; ISO 527-1,-2
80.0 MPa
11600 psi
at yield, 50 mm/min; ISO 527-1,-2
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527-1,-2
24 %
24 %
conditioned, 50 mm/min; ISO 527-1,-2
Tensile Modulus 1.00 GPa
145 ksi
conditioned, 1 mm/min; ISO 527-1,-2
3.20 GPa
464 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 40.0 MPa
5800 psi
conditioned, 2 mm/min; ISO 178-A
105 MPa
15200 psi
2 mm/min; ISO 178-A
Flexural Modulus 1.00 GPa
145 ksi
conditioned, 2 mm/min; ISO 178-A
2.80 GPa
406 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 180-1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 200 kJ/m²

@Temperature -30.0 °C
 95.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 179-1eA
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eA
Puncture Energy 25.0 J

@Temperature -30.0 °C
 18.4 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
55.0 J

@Temperature 23.0 °C
 40.6 ft-lb

@Temperature 73.4 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Melting Point 221 °C
430 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 172 °C
342 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 66.0 °C
151 °F
ISO 75-1,-2
Shrinkage 0.300 %

@Temperature 120 °C,
Time 14400 sec
 0.300 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
0.300 %

@Temperature 120 °C,
Time 14400 sec
 0.300 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer test