Polymer Property : CTE, linear = 8.00 µm/m-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 50.0 °C
4.44 µin/in-°F

@Temperature 68.0 - 122 °F
PCC-Advanced Forming Technology 63% AlSiC Metal Matrix Composite
AlSiC metal matrix composites are formed by pressure infiltrating molten aluminum into silicon carbide preforms. This method of casting is typically used in applications where solution requirements ..
CTE, linear 8.00 µm/m-°C

@Temperature 900 °C
4.44 µin/in-°F

@Temperature 1650 °F
MarkeTech Repton 115 Aluminum Oxide
Brand 115 features: High Density and Purity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even whe..
CTE, linear 8.00 µm/m-°C

@Temperature 900 °C
4.44 µin/in-°F

@Temperature 1650 °F
MarkeTech Repton 136 Aluminum Oxide
Brand 136 features: Molding-structural.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when the..
CTE, linear 8.00 µm/m-°C

@Temperature 300 °C
4.44 µin/in-°F

@Temperature 572 °F
MarkeTech Repton 835 Zirconia + 4 mol% Calcia
Brand 835 features: High porosity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal ..
CTE, linear 8.00 µm/m-°C

@Temperature 900 °C
4.44 µin/in-°F

@Temperature 1650 °F
MarkeTech Repton 835 Zirconia + 4 mol% Calcia
Brand 835 features: High porosity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal ..
CTE, linear 8.00 µm/m-°C

@Temperature 300 °C
4.44 µin/in-°F

@Temperature 572 °F
MarkeTech Repton 837 Zirconia + 4.4 mol% Calcia
Brand 837 features: Good spalling characteristics.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, ev..
CTE, linear 8.00 µm/m-°C

@Temperature 900 °C
4.44 µin/in-°F

@Temperature 1650 °F
MarkeTech Repton 837 Zirconia + 4.4 mol% Calcia
Brand 837 features: Good spalling characteristics.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, ev..
CTE, linear 8.00 µm/m-°C

@Temperature 300 °C
4.44 µin/in-°F

@Temperature 572 °F
MarkeTech Repton 868 Zirconia + 8 mol% Yttria (YSZ)
Brand 868 features: High density.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal c..
CTE, linear 8.00 µm/m-°C

@Temperature 900 °C
4.44 µin/in-°F

@Temperature 1650 °F
MarkeTech Repton EXP 338 Alumina 99.6%
EXP 338 features high porosity.REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal cyc..
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 800 °C
4.44 µin/in-°F

@Temperature 68.0 - 1470 °F
Misumi Alumina 96 Aluminum Oxide, Al2O3
Information provided by MISUMI Corporation.
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 450 °C
4.44 µin/in-°F

@Temperature 68.0 - 842 °F
H.C. Starck WCu 85/15 Tungsten-Copper Composite Material
Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm..
CTE, linear 8.00 - 8.80 µm/m-°C

@Temperature 800 °C
4.44 - 4.89 µin/in-°F

@Temperature 1470 °F
Morgan Advanced Ceramics AL-300â„¢ 97-99% Alumina
Excellent mechanical, thermal, electrical, and chemical properties. Highly versatile grades that can be used for metallized applications.
CTE, linear 8.00 - 8.80 µm/m-°C

@Temperature 800 °C
4.44 - 4.89 µin/in-°F

@Temperature 1470 °F
Morgan Advanced Ceramics Deranoxâ„¢ 970 97-99% Alumina
Excellent mechanical, thermal, electrical, and chemical properties. Highly versatile grades that can be used for metallized applications.
CTE, linear 8.00 - 8.80 µm/m-°C

@Temperature 800 °C
4.44 - 4.89 µin/in-°F

@Temperature 1470 °F
Morgan Advanced Ceramics Deranoxâ„¢ 975 97-99% Alumina
Excellent mechanical, thermal, electrical, and chemical properties. Highly versatile grades that can be used for metallized applications.
CTE, linear 8.00 - 8.80 µm/m-°C

@Temperature 800 °C
4.44 - 4.89 µin/in-°F

@Temperature 1470 °F
Morgan Advanced Ceramics Sintoxâ„¢ CL 97-99% Alumina
Excellent mechanical, thermal, electrical, and chemical properties. Highly versatile grades that can be used for metallized applications.
CTE, linear 8.00 µm/m-°C

@Temperature -30.0 - 70.0 °C
4.44 µin/in-°F

@Temperature -22.0 - 158 °F
Schott F5 Glass
Information Provided by SCHOTT North America, Inc.
CTE, linear 8.00 µm/m-°C

@Temperature -30.0 - 70.0 °C
4.44 µin/in-°F

@Temperature -22.0 - 158 °F
Schott N-BAK2 Glass
Information Provided by SCHOTT North America, Inc.
CTE, linear 8.00 µm/m-°C

@Temperature -30.0 - 70.0 °C
4.44 µin/in-°F

@Temperature -22.0 - 158 °F
Schott N-SF15 Glass
Information Provided by SCHOTT North America, Inc.
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 300 °C
4.44 µin/in-°F

@Temperature 68.0 - 572 °F
Schott N-SSK5 Glass
Information Provided by SCHOTT North America, Inc.
CTE, linear 8.00 µm/m-°C

@Temperature -30.0 - 70.0 °C
4.44 µin/in-°F

@Temperature -22.0 - 158 °F
Schott SF4 Glass
Information Provided by SCHOTT North America, Inc.
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 1000 °C
4.44 µin/in-°F

@Temperature 68.0 - 1830 °F
CeramTec 665 Steatite, MgO•SiO2
Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc..
CTE, linear 8.00 - 9.00 µm/m-°C

@Temperature 20.0 - 1000 °C
4.44 - 5.00 µin/in-°F

@Temperature 68.0 - 1830 °F
CeramTec Frequenta® Steatite
Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. Frequenta® has low dielectric loss, but has be..
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 1000 °C
4.44 µin/in-°F

@Temperature 68.0 - 1830 °F
CeramTec Rubalit® 708S Alumina, 96%
Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste..
CTE, linear 8.00 µm/m-°C

@Temperature 25.0 - 800 °C
4.44 µin/in-°F

@Temperature 77.0 - 1470 °F
ASTM-C372
CoorsTek ADOS-90R 91% Alumina Thick Film Substrate
This 91-percent alumina (nominal) formulation offers a dark brown body for special applications. Applications: thick films and lasers
CTE, linear 8.00 µm/m-°C

@Temperature 25.0 - 800 °C
4.44 µin/in-°F

@Temperature 77.0 - 1470 °F
ASTM-C372
CoorsTek ADS-995 99.5% Alumina Thin Film
Applications: thin film substrates
CTE, linear 8.00 µm/m-°C

@Temperature 25.0 - 1000 °C
4.44 µin/in-°F

@Temperature 77.0 - 1830 °F
ASTM-C372
CoorsTek ADS-995R MidFilm™ 99.5% Alumina Thick Film
Applications: thick films and lasers
CTE, linear 8.00 µm/m-°C

@Temperature 30.0 - 400 °C
4.44 µin/in-°F

@Temperature 86.0 - 752 °F
Ametek Molybdenum-Copper Composite AMC 7525
Information supplied by Ametek Specialty Metal Products.The material is available as finished parts with the following maximum dimensions:Width: 6 inches (152 mm)Thickness: 0.150 inches (3.8 mm)Leng..
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 1000 °C
4.44 µin/in-°F

@Temperature 68.0 - 1830 °F
ASTM-C372
CeramTec CeramCool® Rubalit® 708 Alumina, 96%
CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit..
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 1000 °C
4.44 µin/in-°F

@Temperature 68.0 - 1830 °F
DIN 51045
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance)
Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn..
CTE, linear 8.00 µm/m-°C

@Temperature 100 °C
4.44 µin/in-°F

@Temperature 212 °F
Chevron Phillips Ryton® R10 7006A PPS Polyphenylene Sulfide  (discontinued **)
Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol..