- Crucible Steel 304L Chromium-Nickel Steel
Crucible Steel 304L Chromium-Nickel Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | Crucible Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Crucible Steel 304L Chromium-Nickel Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crucible 304L is a non-hardenable, low carbon austenitic chromium-nickel steel designed for special applications. It is particularly suitable for applications requiring welding operations where it is not practical to anneal after welding . This grade is non magnetic in annealed condition but slightly magnetic when cold worked. Typical applications are screw machine products and all machined parts requiring good corrosion resistance or non-magnetic properties. Information provided by Crucible Specialty Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 7.94 g/cc | 7.94 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 160 | 160 | |
| Tensile Strength, Ultimate | 552 MPa | 80000 psi | |
| Tensile Strength, Yield | 207 MPa @Strain 0.200 % |
30000 psi @Strain 0.200 % |
|
| Elongation at Break | 60 % | 60 % | in 2" |
| Reduction of Area | 70 % | 70 % | |
| Modulus of Elasticity | 193 GPa | 28000 ksi | Tension |
| Izod Impact Unnotched | 149 J | 110 ft-lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.3 µm/m-°C @Temperature 0.000 - 100 °C |
9.60 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 17.8 µm/m-°C @Temperature 0.000 - 316 °C |
9.90 µin/in-°F @Temperature 32.0 - 600 °F |
||
| 18.7 µm/m-°C @Temperature 0.000 - 649 °C |
10.4 µin/in-°F @Temperature 32.0 - 1200 °F |
||
| Specific Heat Capacity | 0.502 J/g-°C @Temperature 0.000 - 100 °C |
0.120 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
| Thermal Conductivity | 16.25 W/m-K @Temperature 93.3 °C |
112.8 BTU-in/hr-ft²-°F @Temperature 200 °F |
|
| 21.6 W/m-K @Temperature 538 °C |
150 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| Melting Point | 1400 - 1420 °C | 2550 - 2590 °F | |
| Solidus | 1400 °C | 2550 °F | |
| Liquidus | 1420 °C | 2590 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 18 - 20 % | 18 - 20 % | |
| Iron, Fe | >= 64.895 % | >= 64.895 % | As Remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Nickel, Ni | 8.0 - 12 % | 8.0 - 12 % | |
| Phosphorous, P | <= 0.045 % | <= 0.045 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000720 ohm-cm @Temperature 23.0 °C |
0.0000720 ohm-cm @Temperature 73.4 °F |