- AK Steel 305 Austenitic Stainless steel
AK Steel 305 Austenitic Stainless steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | AK Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AK Steel 305 Austenitic Stainless steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AK Steel 305 can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is non-magnetic and cannot be hardened by heat treatment. Typical uses include appliances, kitchen utensils, tank covers and other deep drawn parts.Information provided by AK Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.99 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 80 | 80 | Annealed |
| Tensile Strength, Ultimate | 586 MPa | 85000 psi | Annealed |
| Tensile Strength, Yield | 262 MPa @Strain 0.200 % |
38000 psi @Strain 0.200 % |
Annealed |
| Elongation at Break | 50 % | 50 % | in 2 inches, Annealed |
| Modulus of Elasticity | 193 GPa | 28000 ksi | |
| Izod Impact | 140 J | 103 ft-lb | V-Notch (Annealed) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.3 µm/m-°C @Temperature 0.000 - 100 °C |
9.61 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 18.7 µm/m-°C @Temperature <=649 °C |
10.4 µin/in-°F @Temperature <=1200 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C @Temperature 0.000 - 100 °C |
0.120 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
| Thermal Conductivity | 16.2 W/m-K @Temperature 100 °C |
112 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| 21.4 W/m-K @Temperature 500 °C |
149 BTU-in/hr-ft²-°F @Temperature 932 °F |
||
| Melting Point | 1399 - 1454 °C | 2550 - 2649 °F | |
| Solidus | 1399 °C | 2550 °F | |
| Liquidus | 1454 °C | 2649 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 17 - 19 % | 17 - 19 % | |
| Iron, Fe | 64.085 - 73 % | 64.085 - 73 % | As Remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Nickel, Ni | 10 - 13 % | 10 - 13 % | |
| Phosphorous, P | <= 0.045 % | <= 0.045 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000720 ohm-cm | 0.0000720 ohm-cm | |
| Magnetic Permeability | <= 1.02 | <= 1.02 | H = 200 Oersteds, Annealed |