Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 169 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5200 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5240 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5700 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5730 Natural Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of..
Deflection Temperature at 1.8 MPa (264 psi)	76.1 °C @Thickness 6.35 mm	169 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding M5731 Polyvinyl Chloride, Rigid (PVC, Rigid) NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. Dark colored compounds do not..
Deflection Temperature at 1.8 MPa (264 psi)	76.0 °C @Thickness 3.20 mm	169 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® RCY6013 PC+ABS (Asia Pacific) Cycoloy* RCY6013 resin is an injection moldable high flow PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 V0 @ 1.5 mm..
Deflection Temperature at 1.8 MPa (264 psi)	76.2 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm	169 °F @Treatment Temp. 140 °F, Thickness 0.125 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Cellular E2519 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: Physical properties were measured on non-foamed profiles. Measured density of an extruded 1 thick free foamed part was 0.70 gms/cc at a 360 deg.F melt temperature.Information provided by PolyO..
Deflection Temperature at 1.8 MPa (264 psi)	75.9 °C @Thickness 3.18 mm	169 °F @Thickness 0.125 in	Compression Molded, Conditioned at 50 deg.C; ASTM D648
PolyOne Geon™ Vinyl Dry Blend E7506 Polyvinyl Chloride, Rigid (PVC, Rigid) Geon E7506 is recommended for whites and light pastel colors only. Performs well in extrusion blow molding and high rate fencing capstock applications.Physical properties based on Geon E7506 white 1..
Deflection Temperature at 1.8 MPa (264 psi)	76.0 Â°C @Thickness 6.40 mm	169 Â°F @Thickness 0.252 in	Unannealed; ASTM D648
LG Chemical AF312C ABS, Flame Retardant Feature: Injection Molding, Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 79-94-7 and 1309-64-4Information provided by LG Chemical..
Deflection Temperature at 1.8 MPa (264 psi)	76.0 Â°C @Thickness 6.40 mm	169 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL N750 PPE+PS ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical, TV and Business Equipment applications.
Deflection Temperature at 1.8 MPa (264 psi)	76.0 Â°C @Thickness 6.40 mm	169 Â°F @Thickness 0.252 in	unannealed; ASTM D 648
SABIC Innovative Plastics Noryl N750T PPE+HIPS ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical, TV and Business equipment applications.This data was supplied by SABIC-IP for the Americas region.