PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Rigid Molding M5240 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 61.0 cm
24.0 in
Mechanical Properties Metric English Comments
Hardness, Shore D 79
79
ASTM D2240
Tensile Strength, Yield 42.7 MPa
6190 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 45 %
45 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 71.0 MPa
10300 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.18 mm,
Temperature -18.0 °C
3.00 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
Injection Molded; ASTM D256A
3.70 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
6.93 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Injection Molded; ASTM D256A
7.50 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
14.1 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 72.8 °C

@Thickness 6.35 mm
163 °F

@Thickness 0.250 in
Unannealed; ASTM D648
77.8 °C

@Thickness 6.35 mm
172 °F

@Thickness 0.250 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 71.1 °C

@Thickness 6.35 mm
160 °F

@Thickness 0.250 in
Unannealed; ASTM D648
76.1 °C

@Thickness 6.35 mm
169 °F

@Thickness 0.250 in
Annealed; ASTM D648
UL RTI, Electrical 90.0 °C
194 °F
UL 746
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746
UL RTI, Mechanical without Impact 90.0 °C
194 °F
UL 746
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
ALL; UL 94
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
ALL; UL 94
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Descriptive Properties Value Comments
Features General Purpose
High Impact Resistance
Medium Flow
Forms Pellets
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Outdoor Suitability f1
UL 746C; All Colors
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Construction Applications