PolyOne Geon™ Vinyl Dry Blend E7506 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Vinyl Dry Blend E7506 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Geon E7506 is recommended for whites and light pastel colors only. Performs well in extrusion blow molding and high rate fencing capstock applications.Physical properties based on Geon E7506 white 1880.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	78	78	ASTM D2240
Tensile Strength, Yield	43.4 MPa	6290 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.92 GPa	424 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	84.3 MPa	12200 psi	ASTM D790
Flexural Modulus	3.15 GPa	457 ksi	ASTM D790
Izod Impact, Notched	1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Compression Molded; ASTM D256A
Dart Drop Total Energy	57.4 J/cm @Temperature 23.0 °C	0.108 ft-lb/mil @Temperature 73.4 °F	Procedure A, C.125; ASTM D4226
	60.1 J/cm @Temperature 23.0 °C	0.113 ft-lb/mil @Temperature 73.4 °F	Procedure B, C.125; ASTM D4226

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	61.0 µm/m-°C	33.9 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	77.5 °C @Thickness 3.18 mm	172 °F @Thickness 0.125 in	conditioned @ 50 deg.C; ASTM D648
	80.0 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm	176 °F @Treatment Temp. 140 °F, Thickness 0.125 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	75.9 °C @Thickness 3.18 mm	169 °F @Thickness 0.125 in	Compression Molded, Conditioned at 50 deg.C; ASTM D648
	78.3 °C @Thickness 3.18 mm	173 °F @Thickness 0.125 in	Compression Molded, Annealed at 60 deg.C; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	193 - 210 °C	379 - 410 °F

Descriptive Properties	Value	Comments
Features	High Gloss
	Medium Impact Resistance
Forms	Powder
Generic Material	PVC, Rigid
Generic Name	Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method	Extrusion
	Extrusion Blow Molding
PVC Cell Classification	16354	ASTM D1784
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Blow Molding Applications
	Capstock
	Outdoor Applications