Polymer Property : Flexural Strength = 90.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	90.0 MPa @Temperature 125 °C	13100 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 150G / 151G Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact c..
Flexural Strength	90.0 MPa @Temperature 125 °C	13100 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 150G903 Black Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colou..
Flexural Strength	90.0 MPa @Temperature 275 °C	13100 psi @Temperature 527 °F	ISO 178
Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced Product Description:High performance thermoplastic material, 40% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, ..
Flexural Strength	90.0 MPa @Temperature 125 °C	13100 psi @Temperature 257 °F	ISO 178
Victrex® PEEK 90G Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact c..
Flexural Strength	90.0 MPa @Strain 3.50 %	13100 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® B 31 FCS 000000 Nylon 6, Film Grade PA 6, non-reinforced, extrusion, low viscosity, slip agentInformation provided by LANXESS.
Flexural Strength	90.0 MPa @Strain 3.50 %	13100 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® B 35 F 000000 Nylon 6, Extrusion, Low Viscosity PA 6, non-reinforced, extrusion, low viscosity, no additivesInformation provided by LANXESS.
Flexural Strength	90.0 MPa @Temperature 23.0 °C	13100 psi @Temperature 73.4 °F	Practical Use; ASTM-D790
Toyobo GLAMIDE® TY-835TC Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	90.0 MPa @Temperature 23.0 °C	13100 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-422VOR Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	90.0 MPa @Treatment Temp. 150 °C, Time 3600 sec	13100 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m..