Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, 40% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour black.Typical Application Areas:Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
0.25 %

@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
0.45 %

@Temperature 100 °C
0.45 %

@Temperature 212 °F
immersion; ISO 62-1
Viscosity 850000 cP

@Temperature 400 °C
850000 cP

@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
405°C nozzle, 200°C tool; ISO 294-4
Spiral Flow 6.50 cm

@Thickness 1.00 mm
2.56 in

@Thickness 0.0394 in
405°C nozzle, 200°C tool
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 275 °C
9430 psi

@Temperature 527 °F
ISO 527
105 MPa

@Temperature 175 °C
15200 psi

@Temperature 347 °F
ISO 527
175 MPa

@Temperature 125 °C
25400 psi

@Temperature 257 °F
ISO 527
285 MPa

@Temperature 23.0 °C
41300 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 1.5 %

@Temperature 23.0 °C
1.5 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 35.0 GPa

@Temperature 23.0 °C
5080 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 90.0 MPa

@Temperature 275 °C
13100 psi

@Temperature 527 °F
ISO 178
160 MPa

@Temperature 175 °C
23200 psi

@Temperature 347 °F
ISO 178
290 MPa

@Temperature 125 °C
42100 psi

@Temperature 257 °F
ISO 178
380 MPa

@Temperature 23.0 °C
55100 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 30.0 GPa

@Temperature 23.0 °C
4350 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 60.0 MPa

@Temperature 250 °C
8700 psi

@Temperature 482 °F
ISO 604
90.0 MPa

@Temperature 200 °C
13100 psi

@Temperature 392 °F
ISO 604
230 MPa

@Temperature 120 °C
33400 psi

@Temperature 248 °F
ISO 604
360 MPa

@Temperature 23.0 °C
52200 psi

@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear 35.0 µm/m-°C

@Temperature <=143 °C
19.4 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
90.0 µm/m-°C

@Temperature >=143 °C
50.0 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 5.00 µm/m-°C

@Temperature <=143 °C
2.78 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
8.00 µm/m-°C

@Temperature >=143 °C
4.44 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Melting Point 343 °C
649 °F
ISO 11357
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
150 °C
302 °F
Midpoint; ISO 11357
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1e+05
1e+05
1V; ASTM D4496
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 405 °C
761 °F
Mold Temperature 190 - 210 °C
374 - 410 °F
Drying Temperature 120 °C

@Time 18000 sec
248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
Toxicity Index 0.05
NES 713; CO content
0.12
NES 713; CO<sub>2</sub> content
0.17
NES 713; Total gases