Material Notes:

GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-422VOR is a flame resistant, aromatic, and mineral reinforced Nylon-6. It is of halogen origin.23

Physical Properties	Metric	English	Comments
Specific Gravity	1.56 g/cc	1.56 g/cc	Absolute Drying; ASTM-D792
Filler Content	23 %	23 %
Water Absorption	0.50 %	0.50 %	Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium	1.8 %	1.8 %	Absolute Drying; ASTM-D570
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm @Thickness 1.00 mm	0.0010 - 0.0020 in/in @Thickness 0.0394 in	Absolute Drying
	0.0030 - 0.0060 cm/cm @Thickness 3.00 mm	0.0030 - 0.0060 in/in @Thickness 0.118 in	Absolute Drying
Melt Flow	20 g/10 min	20 g/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	Absolute Drying; ASTM-D785
Tensile Strength, Ultimate	24.0 MPa @Temperature 80.0 °C	3480 psi @Temperature 176 °F	Practical Use (Water Absorption 1.8%); ASTM-D638
	28.0 MPa @Temperature 80.0 °C	4060 psi @Temperature 176 °F	Absolute Drying; ASTM-D638
	38.0 MPa @Temperature 23.0 °C	5510 psi @Temperature 73.4 °F	Practical Use (Water Absorption 1.8%); ASTM-D638
	51.0 MPa @Temperature 23.0 °C	7400 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D638
	61.0 MPa @Temperature -40.0 °C	8850 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.8%); ASTM-D638
	65.0 MPa @Temperature -40.0 °C	9430 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D638
Elongation at Break	1.5 %	1.5 %	Absolute Drying; ASTM-D638
	4.5 %	4.5 %	Practical Use (Water Absorption 1.8%); ASTM-D638
Flexural Strength	38.0 MPa @Temperature 80.0 °C	5510 psi @Temperature 176 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	50.0 MPa @Temperature 80.0 °C	7250 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
	63.0 MPa @Temperature 23.0 °C	9140 psi @Temperature 73.4 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	90.0 MPa @Temperature 23.0 °C	13100 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	104 MPa @Temperature -40.0 °C	15100 psi @Temperature -40.0 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Flexural Modulus	1.20 GPa @Temperature 80.0 °C	174 ksi @Temperature 176 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	3.40 GPa @Temperature 80.0 °C	493 ksi @Temperature 176 °F	Absolute Drying; ASTM-D790
	4.40 GPa @Temperature 23.0 °C	638 ksi @Temperature 73.4 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	6.10 GPa @Temperature 23.0 °C	885 ksi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	6.40 GPa @Temperature -40.0 °C	928 ksi @Temperature -40.0 °F	Practical Use (Water Absorption 1.8%); ASTM-D790
	7.20 GPa @Temperature -40.0 °C	1040 ksi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Compressive Strength	45.0 MPa	6530 psi	Practical Use (Water Absorption 1.8%); ASTM-D695
	62.0 MPa	8990 psi	Absolute Drying; ASTM-D695
Izod Impact, Notched	0.300 J/cm @Temperature -40.0 °C	0.562 ft-lb/in @Temperature -40.0 °F	Absolute Drying; ASTM-D256
	0.400 J/cm @Temperature 23.0 °C	0.749 ft-lb/in @Temperature 73.4 °F	Absolute Drying; ASTM-D256
	0.450 J/cm @Temperature -40.0 °C	0.843 ft-lb/in @Temperature -40.0 °F	Practical Use (Water Absorption 1.8%); ASTM-D256
	0.700 J/cm @Temperature 23.0 °C	1.31 ft-lb/in @Temperature 73.4 °F	Practical Use (Water Absorption 1.8%); ASTM-D256
Taber Abrasion, mg/1000 Cycles	32	32	CS-17, Absolute Drying; ASTM-D1044

Thermal Properties	Metric	English	Comments
CTE, linear	42.0 µm/m-°C	23.3 µin/in-°F	Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi)	205 °C	401 °F	Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	160 °C	320 °F	Absolute Drying; ASTM-D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+8 - 1.00e+9 ohm-cm	1.00e+8 - 1.00e+9 ohm-cm	Practical Use (Water Absorption 1.8%); ASTM-D257
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	Absolute Drying; ASTM-D257
Dielectric Strength	20.0 kV/mm @Thickness 2.00 mm	508 kV/in @Thickness 0.0787 in	Practical Use (Water Absorption 1.8%); ASTM-D149
	29.0 kV/mm @Thickness 2.00 mm	737 kV/in @Thickness 0.0787 in	Absolute Drying; ASTM-D149
Arc Resistance	15 sec	15 sec	Practical Use (Water Absorption 1.8%); ASTM-D495
	25 sec	25 sec	Absolute Drying; ASTM-D495
Comparative Tracking Index	350 V	350 V	IEC Method

Processing Properties	Metric	English
Melt Temperature	250 - 285 °C	482 - 545 °F
Mold Temperature	60.0 °C	140 °F
Injection Pressure	40.0 - 60.0 MPa	5800 - 8700 psi