Victrex® PEEK 150G903 Black Polyetheretherketone, Unreinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer Victrex
Trade Name PEEK
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 150G903 Black Polyetheretherketone, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.Typical Application Areas:Complex geometries with thin cross sections or long flow lengths, for high strength and stiffness as well as good ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.45 %

@Temperature 23.0 °C
0.45 %

@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
0.55 %

@Temperature 100 °C
0.55 %

@Temperature 212 °F
ISO 62-1
Viscosity 130000 cP

@Temperature 400 °C
130000 cP

@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
360°C nozzle, 160°C tool; ISO 294-4
Spiral Flow 220 cm

@Thickness 1.00 mm
86.6 in

@Thickness 0.0394 in
365°C nozzle, 160°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 85

@Temperature 23.0 °C
85

@Temperature 73.4 °F
ISO 868
Tensile Strength, Yield 105 MPa

@Temperature 23.0 °C
15200 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 20 %

@Temperature 23.0 °C
20 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.90 GPa

@Temperature 23.0 °C
566 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 13.5 MPa

@Temperature 275 °C
1960 psi

@Temperature 527 °F
ISO 178
20.0 MPa

@Temperature 175 °C
2900 psi

@Temperature 347 °F
ISO 178
90.0 MPa

@Temperature 125 °C
13100 psi

@Temperature 257 °F
ISO 178
175 MPa

@Temperature 23.0 °C
25400 psi

@Temperature 73.4 °F
ISO 178
130 MPa

@Strain 3.50 %
18900 psi

@Strain 3.50 %
ISO 178
Flexural Modulus 4.50 GPa

@Temperature 23.0 °C
653 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 80.0 MPa

@Temperature 120 °C
11600 psi

@Temperature 248 °F
ISO 604
130 MPa

@Temperature 23.0 °C
18900 psi

@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 0.450 kJ/m²

@Temperature 23.0 °C
0.214 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C

@Temperature <=143 °C
30.6 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
140 µm/m-°C

@Temperature >=143 °C
77.8 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature <=143 °C
27.8 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
120 µm/m-°C

@Temperature >=143 °C
66.7 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Specific Heat Capacity 2.20 J/g-°C

@Temperature 23.0 °C
0.526 BTU/lb-°F

@Temperature 73.4 °F
DSC
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.320 W/m-K

@Temperature 23.0 °C
2.22 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
Along flow; ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 156 °C
313 °F
ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
147 °C
297 °F
Midpoint; ISO 11357
Oxygen Index 24 %

@Thickness 0.400 mm
24 %

@Thickness 0.0157 in
ISO 4239
35 %

@Thickness 3.20 mm
35 %

@Thickness 0.126 in
ISO 4239
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm

@Temperature 275 °C
1.00e+9 ohm-cm

@Temperature 527 °F
IEC 60093
1.00e+15 ohm-cm

@Temperature 125 °C
1.00e+15 ohm-cm

@Temperature 257 °F
IEC 60093
1.00e+16 ohm-cm

@Temperature 23.0 °C
1.00e+16 ohm-cm

@Temperature 73.4 °F
IEC 60093
Dielectric Strength 24.0 kV/mm

@Thickness 2.00 mm
610 kV/in

@Thickness 0.0787 in
IEC 60243-1
Comparative Tracking Index 150 V
150 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 365 °C
689 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 °C

@Time 18000 sec
248 °F

@Time 5.00 hour
150 °C

@Time 10800 sec
302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
Toxicity Index 0.074
NES 713; CO content
0.15
NES 713; CO<sub>2</sub> content
0.22
NES 713; Total gases