BASF Ultramid® 8202 L Intermediate PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 8202 L Intermediate PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is available in natural, heat stabilized and pigmented versions. It combines good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance.Applications: gears, fittings, casters, bearings, clips, fasteners, plugs, caps, and filter bowls.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 hour; ASTM D570 |
| 2.7 % | 2.7 % | 50% RH; ASTM D570 | |
| 9.5 % | 9.5 % | Saturation; ASTM D570 | |
| Linear Mold Shrinkage | 0.0305 cm/cm | 0.0305 in/in | 1/8" Bar |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 75.0 MPa @Temperature -40.0 °C |
10900 psi @Temperature -40.0 °F |
ASTM D638 |
| Tensile Strength, Yield | 25.0 MPa @Temperature 121 °C |
3630 psi @Temperature 250 °F |
ASTM D638 |
| 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
ASTM D638 | |
| 79.0 MPa @Temperature 23.0 °C |
11500 psi @Temperature 73.4 °F |
ASTM D638 | |
| 125 MPa @Temperature -40.0 °C |
18100 psi @Temperature -40.0 °F |
ASTM D638 | |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Elongation at Yield | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
|
| 36 % @Temperature 121 °C |
36 % @Temperature 250 °F |
||
| 42 % @Temperature 80.0 °C |
42 % @Temperature 176 °F |
||
| Flexural Strength | 20.0 MPa @Temperature 194 °C |
2900 psi @Temperature 381 °F |
ASTM D790 |
| 20.0 MPa @Temperature 250 °C |
2900 psi @Temperature 482 °F |
ASTM D790 | |
| 30.0 MPa @Temperature 149 °C |
4350 psi @Temperature 300 °F |
ASTM D790 | |
| 110 MPa @Temperature 23.0 °C |
16000 psi @Temperature 73.4 °F |
ASTM D790 | |
| 170 MPa @Temperature -40.0 °C |
24700 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 0.305 GPa @Temperature 121 °C |
44.2 ksi @Temperature 250 °F |
ASTM D790 |
| 0.350 GPa @Temperature 90.0 °C |
50.8 ksi @Temperature 194 °F |
ASTM D790 | |
| 0.500 GPa @Temperature 65.0 °C |
72.5 ksi @Temperature 149 °F |
ASTM D790 | |
| 2.83 GPa @Temperature 23.0 °C |
410 ksi @Temperature 73.4 °F |
ASTM D790 | |
| 3.01 GPa @Temperature -40.0 °C |
437 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ASTM D256 |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C | 46.1 µin/in-°F | ASTM E831 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | ASTM D684 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D684 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 285 °C | 464 - 545 °F | |
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | North America |