Polymer Property : Flexural Strength = 103 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	103 MPa @Temperature 23.9 °C	15000 psi @Temperature 75.0 °F	Dry; 325°F 2500psi and Post-Cure; ASTM D790
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Chopped Molding Compound Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle..
Flexural Strength	103 MPa @Thickness 1.57 mm	15000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP842 Paper Base Laminate (discontinued **) Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP842 is semi-conductive on the surfaces and through the laminate.Thickness Tested: 0..
Flexural Strength	103 MPa @Thickness 1.57 mm	15000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP193P Synthetic Fabric Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temp..
Flexural Strength	103 MPa @Thickness 1.57 mm	15000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M..
Flexural Strength	103 MPa @Thickness 1.57 mm	15000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP315 Cotton Fabric Description: Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions. Material is conductive to electricity and should ..
Flexural Strength	103 MPa @Thickness 1.57 mm	15000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP630 Paper Base Laminate Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500"
Flexural Strength	103 MPa @Temperature 23.0 °C	14900 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-802 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..