Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Nilit FRIANYL A63 W-GV30 Nylon 6.6, std. viscosity for injection molding, 30% glass fiber reinforced Nylon 6.6, std. viscosity for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.70 GPa @Temperature 23.0 °C |
1120 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYshine PBT D221 GF30 PBT, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 7.70 GPa @Temperature 23.0 °C |
1120 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANAMID 66 A33^E F30 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Flexural Modulus | 7.70 GPa @Temperature 23.0 °C |
1120 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANMID 6 B12^ F25 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Nilit FRIANYL A63 H-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Dry, 30% Glass Filled
(discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Europe-Africa-Middle East) LNP* Lubricomp* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP JX00061 PES (Europe-Africa-Middle East) LNP* Lubricomp* JX00061 is a compound based on Polyethersulfone resin containing Carbon Fiber, Proprietary Lubricant. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007U PP (Europe-Africa-Middle East) LNP* VERTON* MV007U is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RFB53SUZ PA 66 LNP THERMOCOMP* RFB53SUZ is a compound based on Nylon 66 resin containing Glass Bead, Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for th.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Plenco 00732 Melamine-Phenolic, Granular, Injection Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Plenco 3554 Phenolic, Granular, Compression Molded PLENCO 03554 is an organic reinforced phenolic molding compound modified with PTFE to offer improved coefficient of friction values. 03554 is available in black. It is UL listed. 03554 is a re-numbe.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Plenco 3557 Phenolic, Granular, Compression Molded PLENCO 03557 is a woodflour and mineral filled phenolic molding compound offering excellent dielectric strength values at elevated temperatures while maintaining mechanical strength properties. UL r.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178-93 |
Wellman Wellamid® MRGF1737-GY1 Nylon 6, 30% Mineral/Glass Reinforced Metallic gray, heat stabilizedAll information provided by Wellman Engineered Resins. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Toyobo T-422-02R Nylon, Mineral-Reinforced Key Feature: High heat distortion and good toughness, high flowInformation provided by Toyobo Co., Ltd |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600 MRGV 20/20 HWCP 20% Mineral and 20% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
DuPont Performance Polymers Crastin® HR5330HF NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)& 30% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5330HF is a 30% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525 Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525 is hydrolysis-resistant, 25% glass-fiber reinforced PA66 resin. Available in natural it is lubricated for improved machine feed and flow. Glass-reinforced Vydyne resins provide higher .. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525H BK0201 Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BK0201 is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525H BLK Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BLK is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® S3 GF 30 1 (3222) PA 6.10 Dry, 30% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK)
(discontinued **) Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6 Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East) VALOX VX4930 is a 30% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525H Nat Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H Nat is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |