SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX VX4930 is a 30% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Filler Content 30 %
30 %
ASTM D229
Moisture Absorption 0.230 %
0.230 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.71 %
0.71 %
ISO 62
Viscosity 130000 cP
130000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
on Tensile Bar; SABIC Method
0.0030 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Flow 13 g/10 min

@Load 3.80 kg,
Temperature 200 °C
 13 g/10 min

@Load 8.38 lb,
Temperature 392 °F
 ASTM D1238
35 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 35 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 ASTM D1238
35 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 35 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 13 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
25 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ISO 2039-2
Hardness, H358/30 210 MPa
30500 psi
ISO 2039-1
Tensile Strength at Break 125 MPa
18100 psi
Type I, 5 mm/min; ASTM D638
130 MPa
18900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 125 MPa
18100 psi
Type I, 5 mm/min; ASTM D638
130 MPa
18900 psi
5 mm/min; ISO 527
Elongation at Break 2.8 %
2.8 %
Type I, 5 mm/min; ASTM D638
2.8 %
2.8 %
5 mm/min; ISO 527
2.9 %
2.9 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.8 %
2.8 %
Type I, 5 mm/min; ASTM D638
2.8 %
2.8 %
5 mm/min; ISO 527
Tensile Modulus 9.50 GPa
1380 ksi
5 mm/min; ASTM D638
9.60 GPa
1390 ksi
1 mm/min; ISO 527
Flexural Strength 180 MPa
26100 psi
2 mm/min; ISO 178
Flexural Yield Strength 175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
185 MPa
26800 psi
2 mm/min; ISO 178
Flexural Modulus 7.70 GPa
1120 ksi
1.3 mm/min, 50 mm span; ASTM D790
8.20 GPa
1190 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature 0.000 °C
 1.50 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.800 J/cm

@Temperature -30.0 °C
 1.50 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 8.00 J/cm
15.0 ft-lb/in
ASTM D4812
8.00 J/cm

@Temperature -30.0 °C
 15.0 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature 0.000 °C
 3.81 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1U
45.0 kJ/m²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
5.50 J/cm²
26.2 ft-lb/in²
ISO 179/2C
2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.900 J/cm²
4.28 ft-lb/in²
ISO 179/2C
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 78.0 J

@Temperature 23.0 °C
 57.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Taber Abrasion, mg/1000 Cycles 65
65
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
22.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 12.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 115 µm/m-°C

@Temperature -40.0 - 40.0 °C
 63.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
115 µm/m-°C

@Temperature 23.0 - 60.0 °C
 63.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.6

@Frequency 50.0 - 60.0 Hz
 3.6

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 21.0 kV/mm

@Thickness 3.20 mm
 533 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0024

@Frequency 50.0 - 60.0 Hz
 0.0024

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0182

@Frequency 1.00e+6 Hz
 0.0182

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
500 V
500 V
IEC 60112