SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ASTM D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 174 MPa
25200 psi
Type I, 5 mm/min; ASTM D 638
190 MPa
27600 psi
5 mm/min; ISO 527
Elongation at Break 2.6 %
2.6 %
Type I, 5 mm/min; ASTM D 638
2.8 %
2.8 %
5 mm/min; ISO 527
Tensile Modulus 8.32 GPa
1210 ksi
1 mm/min; ISO 527
9.30 GPa
1350 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 216 MPa
31300 psi
1.3 mm/min, 50 mm span; ASTM D 790
238 MPa
34500 psi
2 mm/min; ISO 178
Flexural Modulus 6.42 GPa
931 ksi
1.3 mm/min, 50 mm span; ASTM D 790
7.70 GPa
1120 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.23 J/cm

@Temperature 23.0 °C
2.30 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
1.91 J/cm

@Temperature -40.0 °C
3.58 ft-lb/in

@Temperature -40.0 °F
ASTM D 256
Izod Impact, Unnotched 11.6 J/cm

@Temperature 23.0 °C
21.7 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
18.0 kJ/m²

@Temperature -40.0 °C
8.57 ft-lb/in²

@Temperature -40.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 70.0 kJ/m²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af