Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass reinforced PPA. Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly. - Black: AT-1116 HS BK 324 - Natural: AT-1116 HS NTData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183/A
Filler Content 16 %
16 %
Glass Fiber Reinforcement
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.5 MPa

@Temperature 100 °C
9500 psi

@Temperature 212 °F
ISO 527-2
160 MPa

@Temperature 23.0 °C
23200 psi

@Temperature 73.4 °F
ISO 527-2
Tensile Strength 131 MPa
19000 psi
Conditioned; ASTM D638
161 MPa
23400 psi
ASTM D638
Elongation at Break 2.8 %
2.8 %
Conditioned; ASTM D638
3.8 %
3.8 %
ASTM D638
3.7 %

@Temperature 23.0 °C
3.7 %

@Temperature 73.4 °F
ISO 527-2
4.2 %

@Temperature 100 °C
4.2 %

@Temperature 212 °F
ISO 527-2
Tensile Modulus 6.48 GPa
940 ksi
ASTM D638
7.10 GPa
1030 ksi
Conditioned; ASTM D638
6.69 GPa

@Temperature 100 °C
970 ksi

@Temperature 212 °F
ISO 527-2
6.89 GPa

@Temperature 23.0 °C
999 ksi

@Temperature 73.4 °F
ISO 527-2
Flexural Strength 201 MPa
29200 psi
Conditioned; ASTM D790
226 MPa
32800 psi
ASTM D790
141 MPa

@Temperature 100 °C
20500 psi

@Temperature 212 °F
ISO 178
197 MPa

@Temperature 23.0 °C
28600 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 6.00 GPa
870 ksi
ASTM D790
6.21 GPa
901 ksi
Conditioned; ASTM D790
4.96 GPa

@Temperature 100 °C
719 ksi

@Temperature 212 °F
ISO 178
6.69 GPa

@Temperature 23.0 °C
970 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 124 MPa
18000 psi
ASTM D695
Shear Strength 65.5 MPa
9500 psi
Conditioned; ASTM D732
69.6 MPa
10100 psi
ASTM D732
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
Conditioned; ASTM D256
0.960 J/cm
1.80 ft-lb/in
ASTM D256
8.00 J/cm
15.0 ft-lb/in
Conditioned; ASTM D256
9.60 J/cm
18.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²

@Temperature 23.0 °C
25.2 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 8.60 J/cm²
40.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy 7.59 J
5.60 ft-lb
Conditioned; ASTM D3763
10.0 J
7.38 ft-lb
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.0 µm/m-°C

@Temperature 100 - 200 °C
8.89 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
22.0 µm/m-°C

@Temperature 0.000 - 100 °C
12.2 µin/in-°F

@Temperature 32.0 - 212 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature 0.000 - 100 °C
41.7 µin/in-°F

@Temperature 32.0 - 212 °F
ASTM E831
120 µm/m-°C

@Temperature 100 - 200 °C
66.7 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
Melting Point 310 °C
590 °F
Peak; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 268 °C
514 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 254 °C
489 °F
Annealed; ASTM D648
258 °C
496 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 110 °C
230 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Impact Modifier
Appearance Black
Natural Color
Automotive Specifications ASTM D4000 PPA0111 G17 KD124 KN055 PN046 YI238 LD002 Color: BK 324 and NT Black and Natural
ASTM D6779 PA123G15 YI220
GM GMN6828
GM GMN6828 Color: BK 324 and NT Black and Natural
GM GMP.PPA.009 Color: BK 324 and NT Black and Natural
ISO 1874-PA 6T/6I/66-HI, MH, 12-060, GF16
YAZAKI YPES-25-02-305 Color: BK 324 and NT Black and Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Dimensional Stability
Heat Stabilized
High Heat Resistance
Impact Modified
Forms Pellets
Generic PPA
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Automotive Under the Hood
Bearings
Bobbins
Connectors
General Purpose
Industrial Applications
Industrial Parts
Machine/Mechanical Parts
Metal Replacement