Polymer Property : Flexural Modulus = 1230 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 3414R PC (Europe-Africa-Middle East)
LEXAN 3414R is a high viscosity, 40% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance.
Flexural Modulus 8.50 GPa

@Temperature 23.0 °C
1230 ksi

@Temperature 73.4 °F
ISO 178
Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced
Product Description:High performance thermoplastic material, 20% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta..
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
LNP Lubricomp® EFL-4544 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant  (discontinued **)
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Hexion Bakelite™ PF 1141 Phenolic Formaldehyde Resin, High Surface Quality, Resistant to High Temperatures, Dishwasher Proof
Phenolic molding compound, inorganically/organically filled, glass fiber reinforced, increased heat resistance, hot steam and hot water resistant (not suitable for use of higher voltage).Application..
Flexural Modulus 8.50 GPa
1230 ksi
Lehmann & Voss LUVOCOM® 1105-7776 PEEK, with carbon fiber, lubricant modified
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Low warpage, isotropic shrinkage characteristics.Emergency running pro..
Flexural Modulus 8.50 GPa
1230 ksi
Lehmann & Voss LUVOCOM® 1105-7907 PEEK, with carbon fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts at high movement velocity.High chemical resista..
Flexural Modulus 8.50 GPa
1230 ksi
Lehmann & Voss LUVOCOM® 1-8501 Polyamide 66, with glass fiber, lubricant modified, heat stabilized
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.dynamic st..
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Lanxess Durethan® AKV 30 H3.0 000000 Nylon 66, 30% Glass Fibers
PA 66, 30% glass fibers, injection molding, heat-ageing stabilized
Flexural Modulus 8.50 GPa
1230 ksi
Lehmann & Voss LUVOCOM® 1-0936 Polyamide 66, with glass fiber and PTFE, 8-mm-granulate
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Flexural Modulus 8.50 GPa
1230 ksi
2mm/min; ASTM D790
Kingfa PA66-G30 30% Glass Fiber Reinforced PA66
Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
Flexural Modulus 8.50 GPa
1230 ksi
ASTM D790
IRPC Polimaxx Polene 1111NX GA6 Polypropylene Compound
CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 30% GLASS FIBRE REINFORCED HIGH IMPACT STRENGTH, HIGH MECHANICAL STRENGTH, HIGH STIFFNESS LOW SHRINKAGEAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ..
Flexural Modulus 8.45 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp EFP36G PEI
LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2300F PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2300F PEI (Europe-Africa-Middle East)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. US FDA and European Food Contact compliant. Effective June, 2007 this grade will no longer be supported with ..
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2300R PEI (Europe-Africa-Middle East)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant. UL94 V0 and 5VA listing.
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
SABIC Innovative Plastics LNP Lubriloy RF206H PA 66
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant, Lubricants. Added features of this material include: Internally Lubricated.This data was su..
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific)
VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin..
Flexural Modulus 8.50 GPa
1230 ksi
SPS Guang Zhou POBUXâ„¢ 3001EPG30 Non-halogen flame retardance/GF30%-PBT
Characteristic: Good flame retardance, high mechanical properties, high rigidity, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) ..
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
Techmer ES Luriblend® PA6/6 GF30 TS1 BK 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear R..
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East)
LNP* THERMOCOMP* DX06094 is a compound based on Polycarbonate resin containing Glass Fiber . Added features include: High Impact, Non- Brominated & Non-Chlorinated Flame Retardant and Mold Release...
Flexural Modulus 8.50 GPa
1230 ksi
ASTM D790
Plenco 4599 Phenolic, Granular, Injection Molded
PLENCO 04599 is a mineral filled, phenolic molding compound offering excellent heat resistance and dimensional stability, typically required for automotive ashtray applications. 04599 is formulated ..
Flexural Modulus 8.50 GPa
1230 ksi
dry; ISO 178
DSM Stanyl® TW271F6J10 (PA46+PTFE)-GF30
30% Glass Reinforced, Heat Stabilized, Wear and Friction Modified
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Eurotec® Tecomid® NB40 GR30 NL PA 6 30% glass fiber reinforced
Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Flexural Modulus 8.50 GPa
1230 ksi
ASTM D790
E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM
GF reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
Celanese CELANEX 3309HRLM PBT, 30% Glass Reinforced
Celanex 3309HRLM is a non-lubricated, 30% fiberglass reinforced Polybutylene Terephthalate which has excellent hydrolysis resistance, mechanical properties and processability. lIt is a asermarkable ..
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Celanese Celstran® PPS-AF35-01- PPS, 35% Aramid Reinforced
PPS with 35% aramid fiber by weightInformation provided by Celanese
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
RTP Company RTP 205D  Nylon 6/12 (PA 6/12) Glass Fiber 30%  (discontinued **)
Glass Fiber 30%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Celanese Hostaform® EC140CF10 POM, 10% Specialty  (Unverified Data**)
Hostaform® acetal copolymer grade EC140CF10 is a 10% carbon fiber reinforced grade for increase strength, stiffness and electrical conductivity.10% carbon fiber, electrostatic dissipative gradeInfo..
Flexural Modulus 8.50 GPa
1230 ksi
ASTM D790
Plenco 4485 Phenolic, Granular, Transfer Molded
PLENCO 04485 is a mineral filled phenolic molding compound offering excellent heat resistance, electrical resistance, and dimensional stability. UL recognized under component file E40654. 04485 is a..
Flexural Modulus 8.50 GPa
1230 ksi
Lehmann & Voss LUVOCOM® 1-7233-1 Polyamide 66, with glass fiber, PTFE, lubricant modified, silicone-free
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, ..