SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFG16S is a compound based on Nylon 66 resin containing 5% Graphite, 30% Glass Fiber. Added features of this material include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.900 % | 0.900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
| 169 MPa | 24500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
| 169 MPa | 24500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.63 GPa | 1400 ksi | 1 mm/min; ISO 527 |
| 11.24 GPa | 1630 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 232 MPa | 33600 psi | ISO 178 |
| 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 234 MPa | 33900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.38 GPa | 1220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.45 GPa | 1230 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Unnotched | 6.85 J/cm | 12.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.37 | 0.37 | ASTM D3702 Modified |
| K (wear) Factor | 286 x 10-8 mm³/N-M | 142 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 66.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following: