|Shear Strength||42.0 - 76.0 MPa||6090 - 11000 psi||Average value: 58.9 MPa Grade Count:7|
|Overview of materials for Nylon 66, 10% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. ..
|Shear Strength||68.9 - 75.8 MPa||10000 - 11000 psi||ASTM D732|
|Mar-Bal MB1000-PC Thermoset Polyester Composite Molding Compound
A general purpose material that is easily customized. Designed for Powder Coating and Electrostatic painting.Mar-Bal standard grades can be injection, compression and transfer molded.Information pro..
|Shear Strength||62.1 - 75.8 MPa||9000 - 11000 psi||ASTM D732|
|Mar-Bal MB2000-20 Thermoset Polyester Composite Molding Compound
An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can..
|Shear Strength||66.0 - 76.0 MPa||9570 - 11000 psi||2mm/min.; IS 867-1963|
|Amity Thermosets ATM 144 Phenolic Molding Organic Filler, Compression Molded
Characteristics:Good mouldability Good mechanical strengthGood electrical insulationGood surface finishMedium thermal stabilityColor- black, brownSoft/medium flow Applications: Electric control pane..
|Shear Strength||44.8 - 75.8 MPa||6500 - 11000 psi||Average value: 66.3 MPa Grade Count:15|
|Overview of materials for Nylon 6, Cast
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW..