Polymer Property : Tensile Strength, Ultimate = 89.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
Nylene® Naxel™ PC504 20% Glass Reinforced Polycarbonate
Description: Naxel™ PC504 is a 20% glass fiber reinforced polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resourc..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
Nylene® Vexel™ B12GF15 , 15% Glass Reinforced PBT
Description: Vexel™ B12GF15 is a 15% glass fiber reinforced, general purpose PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeri..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PS-15GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated  (discontinued
Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 HB (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4000 AR 15 TFE 10  Polyphthalamide (PPA) Aramid Fiber 15% - PTFE 10%  (disco
Aramid Fiber 15% - PTFE 10%Comments:Aramid FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provi..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4001 FR  Polyphthalamide (PPA) Glass Fiber 10% - Flame Retardant  (discontin
Glass Fiber 10% - Flame RetardantComments:Glass FiberFlame RetardantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information ..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4001A  Polyphthalamide - Hot Water Mold (PPA) Glass Fiber 10%  (discontinued
Glass Fiber 10%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PK-5GP/7T Polyetheretherketone (PEEK), PTFE Lubricated  (discontinued **)
Description/Features:Graphite LubricatedPTFE LubricatedInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® AS-20CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced  (discontinued **)
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced  (discontinued **)
Description/Features:Electrically ConductiveNickel Coated Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 1803  Acrylic (PMMA) Glass Fiber 20%  (discontinued **)
Glass Fiber 20%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 2100 AR 15 TFE 15 Z  Polyetherimide (PEI) Aramid Fiber 15% - PTFE 15% - FDA Type &
Aramid Fiber 15% - PTFE 15% - FDA TypeComments:Aramid FiberPTFE LubricatedFDA CompliantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect prop..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 2100 HF  Polyetherimide (PEI) High Flow  (discontinued **)
High FlowComments:High FlowUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for this pro..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 200G  Nylon 4/6 (PA 4/6) Base Resin  (discontinued **)
Base ResinComments:Unfilled(Dry As Molded)Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Th..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 205C  Nylon 11 (PA 11) Glass Fiber 30%  (discontinued **)
Glass Fiber 30%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 201D L  Nylon 6/12 (PA 6/12) Glass Fiber 10% - Lubricated  (discontinued **)
Glass Fiber 10% - LubricatedComments:Glass FiberLubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided b..
Tensile Strength, Ultimate 89.6 MPa

@Temperature 482 °C
13000 psi

@Temperature 900 °F
Monel butt joint
Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal
Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
Applied Composites 179 Polyester SMC
Industry Application: TransportationProduct Application: Auto InteriorsInformation provided by Applied Composites Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
Applied Composites 8007 Polyester SMC
Industry Application: ConstructionProduct Application: Water TreatmentDistinct Features: Pigmentable, Low Water Absorption, Weathering Resistant, Good Corrosion Resistance in Waste Water Environment..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 201D GB 20  Nylon 6/12 (PA 6/12) Glass Fiber 10% - Glass Bead 20%  (disconti
Glass Fiber 10% - Glass Bead 20%Comments:Glass FiberGlass BeadUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provid..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4200  Thermoplastic Polyimide (TPI) Base Resin  (discontinued **)
Base ResinComments:UnfilledUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for this pro..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4299 X 93109  Thermoplastic Polyimide (TPI) Electronic Encapsulation  (disc
Electronic EncapsulationComments:Encapsulation GradeUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP ..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4000 AR 15 TFE 13 SI 2  Polyphthalamide (PPA) Aramid Fiber 15% - PTFE 13% - Silicone 2%
Aramid Fiber 15% - PTFE 13% - Silicone 2%Comments:Aramid FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4000A AR 15 SI 2  Polyphthalamide - Hot Water Mold (PPA) Aramid Fiber 15% - Silicone 2%
Aramid Fiber 15% - Silicone 2%Comments:Aramid FiberSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Informatio..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 4000A AR 15 TFE 15 SI 2  Polyphthalamide - Hot Water Mold (PPA) Aramid Fiber 15% - PTFE 15% - Silicone 2%
Aramid Fiber 15% - PTFE 15% - Silicone 2%Comments:Aramid FiberPTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can af..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ RA-15GF/13T Polyethersulfone, Glass Filled, PTFE Lubricated  (discontinued **)
Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 V0UL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 1402 N Z  Polyethersulfone (PES) Glass Fiber 15% - FDA Type - High Viscosity &nbs
Glass Fiber 15% - FDA Type - High ViscosityComments:Glass FiberFDA CompliantHigh ViscosityUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect p..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 1782  Modified Polyphenylene Oxide (PPO) Carbon Fiber 15%  (discontinued **)
Carbon Fiber 15%Comments:Carbon FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data fo..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced
Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate 89.6 - 245 MPa
13000 - 35500 psi
Average value: 172 MPa Grade Count:24
Overview of materials for Polyphthalamide (PPA), Glass/PTFE
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide + Glass/PTFE". Each property range of values reported is minimum and maximum values of a..
Tensile Strength, Ultimate 89.6 MPa
13000 psi
ASTM D638
RTP Company RTP 1705 Z  Modified Polyphenylene Oxide (PPO) Glass Fiber 30%  (discontinued **
Glass Fiber 30%Comments:Glass FiberFDA CompliantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Comp..
Copyright © lookpolymers.com All Rights Reserved