Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 10% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.26 - 1.65 g/cc
0.0455 - 0.0596 lb/in³
Average value: 1.48 g/cc Grade Count:12
Filler Content 10.0 %
10.0 %
Average value: 10.0 % Grade Count:6
Water Absorption 0.120 - 0.300 %
0.120 - 0.300 %
Average value: 0.240 % Grade Count:6
Linear Mold Shrinkage 0.00100 - 0.0150 cm/cm
0.00100 - 0.0150 in/in
Average value: 0.00625 cm/cm Grade Count:9
Melt Flow 5.00 - 50.0 g/10 min
5.00 - 50.0 g/10 min
Average value: 22.7 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122 - 125
122 - 125
Average value: 124 Grade Count:5
Tensile Strength, Ultimate 89.6 - 125 MPa
13000 - 18100 psi
Average value: 100 MPa Grade Count:8
Tensile Strength, Yield 98.1 - 216 MPa
14200 - 31300 psi
Average value: 145 MPa Grade Count:4
Elongation at Break 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 1.88 % Grade Count:10
Modulus of Elasticity 5.52 - 9.17 GPa
800 - 1330 ksi
Average value: 6.83 GPa Grade Count:7
Flexural Yield Strength 131 - 275 MPa
19000 - 39900 psi
Average value: 160 MPa Grade Count:12
Flexural Modulus 4.83 - 13.2 GPa
700 - 1920 ksi
Average value: 7.27 GPa Grade Count:12
Izod Impact, Notched 0.267 - 1.23 J/cm
0.500 - 2.30 ft-lb/in
Average value: 0.432 J/cm Grade Count:11
Izod Impact, Unnotched 2.14 - 3.20 J/cm
4.00 - 6.00 ft-lb/in
Average value: 2.76 J/cm Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 20.0 - 20.0 µm/m-°C

@Temperature 160 - 249 °C
11.1 - 11.1 µin/in-°F

@Temperature 320 - 480 °F
Average value: 20.0 µm/m-°C Grade Count:1
CTE, linear, Transverse to Flow 65.0 - 65.0 µm/m-°C

@Temperature 160 - 249 °C
36.1 - 36.1 µin/in-°F

@Temperature 320 - 480 °F
Average value: 65.0 µm/m-°C Grade Count:1
Deflection Temperature at 1.8 MPa (264 psi) 168 - 295 °C
335 - 563 °F
Average value: 245 °C Grade Count:12
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:8
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Average value: 1.00e+15 ohm-cm Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 296 - 338 °C
565 - 640 °F
Average value: 321 °C Grade Count:3
Melt Temperature 280 - 343 °C
536 - 650 °F
Average value: 316 °C Grade Count:5
Mold Temperature 65.6 - 163 °C
150 - 325 °F
Average value: 129 °C Grade Count:8
Drying Temperature 107 - 140 °C
225 - 284 °F
Average value: 114 °C Grade Count:5
Moisture Content 0.0500 - 0.100 %
0.0500 - 0.100 %
Average value: 0.0820 % Grade Count:5
Dew Point -31.7 - -28.9 °C
-25.0 - -20.0 °F
Average value: -29.8 °C Grade Count:3
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 89.6 MPa Grade Count:6