Polymer Property : Tensile Strength, Ultimate = 6000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.4 MPa
6000 psi
Mykroy/Mycalex MM 500 Machining Grade Glass-bonded Mica Composite
Synthetic mica filler. Does not burn. Better radiation resistance (3 x 10^10 Rads-Cobalt) than grade 400.This ceramoplastic material is a versatile and efficient insulating material designed to me..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D412
5265 Polyurethane-based Biomedical Elastomer
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D412
5286 Polyurethane-based Biomedical Elastomer
Tensile Strength, Ultimate 41.4 - 126 MPa
6000 - 18300 psi
Average value: 65.7 MPa Grade Count:18
Overview of materials for Polyphenylene Ether, Heat Resistant
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Heat Resistant". Each property range of values reported is minimum and maximum valu..
Tensile Strength, Ultimate 41.4 - 79.3 MPa
6000 - 11500 psi
Average value: 64.1 MPa Grade Count:5
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant". Each property range of valu..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
RTP Company PermaStat® 1800A FR  Polycarbonate/Acrylic Alloy (PC/PMMA) Anti-Static - Flame Retardant
Anti-Static - Flame RetardantComments:Permanently Anti-StaticESD ProtectionFlame RetardantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect p..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
RTP Company RTP 3102  Perfluoroalkoxy (PFA) Glass Fiber 15%  (discontinued **)
Glass Fiber 15%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for ..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
RTP Company RTP 200F TFE 20  Nylon 12 (PA 12) PTFE 20%  (discontinued **)
PTFE 20%Comments:PTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for thi..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM Data
Styron Magnumâ„¢ 341 ABS, Low Gloss
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
Williams Advanced Alloys WS212 Solder
All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D412
Lubrizol Estane® ALR PC85A Thermoplastic Polyurethane
Type: Estane® ALR PC85A is a polycarbonate diol based thermoplastic polyurethane (TPU).Features: Hydrolytically stable, very durableAvailable in Americas, Europe, Middle East, Africa, India and Asi..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D412
Lubrizol Estane® 2355-55DE Thermoplastic Polyurethane
Type: Pellethane® 2355-55DE is a thermoplastic polyurethane elastomer.Information Provided by The Lubrizol Corporation
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
Ecomass® 1080BI64 Filled Polyamide
Nontoxic alternative compound for weighting, balancing and radiation shielding applicationsModerate Specific GravityFilled Polyamide (PA) AlloyExcellent ToughnessInformation provided by Technical Po..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
Ecomass® 1080TU95 Tungsten Filled Polyamide
Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Powder Filled Polyamide (PA) AlloyExcellent ToughnessInformation provided b..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
Ecomass® 1080ZD94 Tungsten Filled Polyamide
Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications.High Specific GravityTungsten Filled Polyamide (PA) AlloyExcellent ToughnessInformation provided by Techn..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D1708
DSM Biomedical BioSpan® SPU Segmented Polyether Polyurethane (SPU)
The flex life exhibited by BioSpan® SPU enables good performance in many different types of medical devices. This elastomeric polymer has shown the ability to withstand millions of flex cycles.The ..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
Dymax 9-984-B Conformal Coating
High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9-984-B Conformal CoatingCures to an opaque black finish; hides components or circuitry from view; protects sensitiv..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ETFE film property; ASTM D638
Arlon 25188T017 Silicone Rubber/Laminated ETFE Film
Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
Buckeye Polymers BP ABS 4332 ABS
Low GlossABS is a copolymer of acrylonitrile and styrene, modified with butadiene rubber. ABS is primarily used for their combination of toughness, rigidity, chemical resistance, ease of processing..
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Bulk Molding Compounds BMC 605L Mineral Filled, Glass Fiber Reinforced Polyester Compound
BMC 605L molding compound is a low cost, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is characterized by good molda..
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Bulk Molding Compounds BMC 605LS Mineral Filled, Glass Fiber Reinforced Polyester Compound
BMC 605LS molding compound is a low-shrink, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good mol..
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Bulk Molding Compounds BMC 800 Thermoset Polyester, Corrosion Resistant
BMC 800 compounds are UL rated 94V0/5V. These compounds exhibit excellent strength, corrosion and weather resistant properties. As with all other BMCI compounds, this Series can be supplied in logs,..
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Bulk Molding Compounds BMC 880 Medium Strength Molding Compound
BMC 880 is a medium strength, low shrink molding compound designed for outdoor applications. This material is UL Listed 94-V0/5V and is UL approved for outdoor use. It can be supplied in bulk or ext..
Tensile Strength, Ultimate 41.4 - 48.3 MPa
6000 - 7000 psi
Bulk Molding Compounds BMC 1412 Flame and Track Resistant
BMC 1412 is an extremely versatile material. Flame and track resistant, low shrink for close dimensional control and surface smoothness, high physical properties. Developed for injection molding, bu..
Tensile Strength, Ultimate 41.4 - 55.2 MPa
6000 - 8000 psi
Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound
BMC 605 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, medi..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
Dymax 3086 Solvent-Free Plastic Adhesive
Solvent-Free Adhesives for Plastic Assembly in SecondsDymax® Light-Weld® and Ultra 3000 Series UV and UV/Visible Curing Adhesives for plastic assembly provide instant durable bonds to cure a wide ..
Tensile Strength, Ultimate 41.4 - 64.0 MPa
6000 - 9280 psi
Average value: 53.1 MPa Grade Count:22
Overview of materials for Acetal Homopolymer, PTFE-Filled
This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, PTFE-Filled". Each property range of values reported is minimum and maximum values o..
Tensile Strength, Ultimate 41.4 - 61.0 MPa
6000 - 8850 psi
Average value: 49.7 MPa Grade Count:22
Overview of materials for Acrylic/Polycarbonate Alloy
This property data is a summary of similar materials in the MatWeb database for the category "Acrylic/Polycarbonate Alloy". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
TM R050-36
Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin
Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C..
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D412
RTP Company RTP 1203-65D  Polyurethane Thermoplastic Elastomer (TPU) Glass Fiber 20% - 65 Shore D &am
Glass Fiber 20% - 65 Shore DComments:Glass Fiber65-D DurometerUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provid..